Título: Microfiltración in vitro del sellado apical de conductos radiculares empleando 2 cementos endodónticos
Asesor(es): Espinoza Salcedo, María Victoria
Fecha de publicación: 2014
Institución: Universidad Privada Antenor Orrego - UPAO
Resumen: El presente estudio es de tipo experimental cuyo objetivo fue comparar la microfiltración in vitro en el sellado apical de conductos radiculares empleando cementos endodónticos a base de resina epóxica (Adseal) y a base de hidróxido de calcio (Sealapex). Se recolectaron 42 premolares monorradiculares recientemente extraídas para el estudio a las cuales se les realizó tratamiento de conducto y se obturaron con dos cementos endodónticos diferentes, dividiendóse en 4 grupos: Grupo A conformado por 17 premolares monorradiculares con el cemento endodóntico a base de resina epóxica (Adseal), grupo B conformado por 17 premolares monorradiculares a base de hidróxido de calcio (Sealapex); grupo C control positivo conformado por 4 premolares que fueron piezas instrumentadas sin obturar y permeables los 2 mm más apicales y por último el grupo D control negativo conformado por 4 premolares a los cuales se les instrumentó e impermeabilizó con barníz de uñas en su totalidad. Posteriormente todas las piezas fueron sumergidas en tinta china, luego fueron sometidas al proceso de diafanización según la técnica de Robertson. El cemento endodóntico a base de resina epóxica (Adseal) presentó un promedio de 1.28mm y desv. est. de 0.49 y el cemento endodóntico a base de hidróxido de calcio (Sealapex )presentó un promedio de 1.94mm y desv. est. de 0.51. Concluyendo que existe menor microfiltración con el cemento endodóntico a base de resina epóxica (Adseal) en comparación del cemento endodóntico a base de hidróxido de calcio (Sealapex).

This study is experimental type whose objective was to compare vitro microleakage in the apical seal of root canal endodontic resin cements using Epoxy (Adseal) and based calcium hydroxide (Sealapex). Were collected monoradiculars premolars 42 recently extracted for the study which was perfomed in root canal treatment and preparation with two cement various endodontic, splitting into 4 groups: Group A consisting of monoradiculars premolars 17 with cement-based resin endodontic Epoxy (Adseal), Group B consisting of monoradiculars premolars 17 calcium hydroxide-based (Sealapex), Group C monoradiculars positive control consisting of premolars 4 that were instrumented parts without seal and permeable 2mm more apical and finally the Group D negative control consisting of monoradiculars premolars 4 is implemented them proofed with nail lacquer in its entirety. All the pieces were immersed in Chinese ink and then they were subjected to the process of diaphanization according to the technique of Robertson. Cement based_resin endodontic epoxy (Adseal) presented an average of 1.28mm and deviation standard of 0.49 and endodontic cement calcium hydroxide (Sealapex) showed an average of 1.94 and deviation standard of 0.51. Concluding that there is less microleakage with cement-based resin endodontic Epoxy (Adseal) unlike cement endodontic-based calcium hydroxide (Sealapex).
Disciplina académico-profesional: Estomatología
Institución que otorga el grado o título: Universidad Privada Antenor Orrego. Facultad de Medicina Humana
Grado o título: Cirujano Dentista
Fecha de registro: 3-sep-2015



IMPORTANTE
La información contenida en este registro es de entera responsabilidad de la universidad, institución o escuela de educación superior que administra el repositorio académico digital donde se encuentra el trabajo de investigación y/o proyecto, los cuales son conducentes a optar títulos profesionales y grados académicos. SUNEDU no se hace responsable por los contenidos accesibles a través del Registro Nacional de Trabajos de Investigación – RENATI.