Título: Propuesta para el mejoramiento de la calidad estructural del ladrillo artesanal adicionando viruta de acero en la ciudad de Chiclayo
Asesor(es): Villanueva Maguiña, Ronald Esteban
Campo OCDE: http://purl.org/pe-repo/ocde/ford#2.01.00
Fecha de publicación: 2024
Institución: Universidad Católica Santo Toribio de Mogrovejo
Resumen: El presente proyecto fue desarrollado con el objetivo de proponer una alternativa de unidad de albañilería artesanal, con la utilización de viruta de acero como un componente dentro de su fabricación tradicional en la ciudad de Chiclayo. Iniciando se obtuvo las materias primas como la tierra arcillosa, arena fina y la viruta propiamente dicha, que son residuos de tornos y talleres, para poder determinar sus propiedades físico-químicas. Posteriormente se desarrolló un diseño de mezclas para unidades tradicionales y unidades adicionadas con viruta de acero al 8%, 10% y 12% que nos permite poder elaborar unidades de albañilería adicionados de viruta de acero. A continuación, se procedió a realizar los ensayos a las unidades de albañilería, pilas y muretes. Los ensayos fueron realizados de acuerdo a la Norma E0.70 de Albañilería y mediante la NTP 399.613 se demostró que las propiedades de absorción, variación dimensional, alabeo, peso por unidad de área y eflorescencia son aceptables en unidades de albañilería adicionadas con viruta de acero al 10%, así mismo su resistencia a la compresión fue superior a la muestra patrón con un valor de 127.12kg/cm2, por lo anteriormente mencionado esta unidad sería clasificado como un ladrillo Tipo IV según el RNE. En ensayos realizados a prismas y muretes siguiendo las recomendaciones de la NTP 399.605 y NTP 399.621, superaron la resistencia mínima para muros portantes. En conclusión, la unidad de albañilería con adición de 10% de viruta de acero sería una solución económica y con resistencias aceptables por la Norma E0.70 de Perú.

This project was developed with the aim of proposing an alternative craft masonry unit, with the use of steel shavings as a component within its traditional manufacture in the city of Chiclayo. Initially, raw materials such as clay earth, fine sand and shavings were obtained, which are residues of lathes and workshops, in order to determine their physicochemical properties. Subsequently, a blend design was developed for traditional units and units added with 8%, 10% and 12% steel chip, which allows us to produce masonry units added with steel chip. Tests were then carried out on the masonry units, batteries and bricks. The tests were carried out according to the Masonry Standard E0. 70 and by means of the NTP 399. 613 it was demonstrated that the properties of absorption, dimensional variation, bending, weight per unit area and efflorescence are acceptable in masonry units added with 10% steel chip, as well as their compressive strength was superior to the sample. with a value of 127. 12kg/cm2, therefore this unit would be classified as a Type IV brick according to the RNE. In tests carried out on prisms and bricks following the recommendations of NTP 399. 605 and NTP 399. 621, they exceeded the minimum strength for load-bearing walls. In conclusion, the masonry unit with the addition of 10% of steel chip would be an economical solution and with acceptable strengths according to the Peruvian Standard E0. 70.
Disciplina académico-profesional: Ingeniería Civil Ambiental
Institución que otorga el grado o título: Universidad Católica Santo Toribio de Mogrovejo. Facultad de Ingeniería
Grado o título: Ingeniero Civil Ambiental
Jurado: Cespedes Deza, Jose Alfredo Rolando; Acero Martinez, Jose Alberto; Villanueva Maguiña, Ronald Esteban
Fecha de registro: 15-ene-2024



Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons Creative Commons