Buscar en Google Scholar
Título: Influencia del uso del agregado reciclado con parámetros controlados sobre la resistencia a compresión del concreto en la ciudad de Trujillo, La Libertad 2019.
Asesor(es): Villar Quiroz, Josualdo Carlos
Campo OCDE: https://purl.org/pe-repo/ocde/ford#2.01.01
Fecha de publicación: 2020
Institución: Universidad Privada de Trujillo
Resumen: La presente investigación se realizó en la Universidad Privada de Trujillo, se determinó la resistencia a la compresión de probetas de concreto reciclado con parámetros controlados. En esta investigación se explica la influencia del porcentaje y tamaño máximo nominal de concreto reciclado como sustituyente del agregado grueso, sobre la resistencia a la compresión de un concreto reciclado; a base de un cemento portland Tipo I. Los porcentajes de concreto reciclado adicionados fueron de 0%, 10%, 20 %, 30 %, 40% y 50 %, para tamaños máximos nominales del agregado grueso, y usando una relación agua/cemento de 0.56 con una resistencia de diseño de 210 kg/cm3. Se elaboró el diseño de mezcla en base a la caracterización de los materiales del concreto según método ACI 211, en estado fresco para el concreto: se realizó el ensayo de peso unitario según ASTM C 138, densidad del concreto (expresado en kg/cm3), luego se elaboraron 36 probetas (de 15 cm de diámetro y 30 cm de alturas) y se sometieron a curado por inmersión en agua durante 28 días según ASTM C 31, luego en estado endurecido para el concreto reciclado: se realizó el ensayo de resistencia a la compresión según ASTM C 39 para la determinación de la carga que soportará este concreto (expresada en kg/cm2), el problema es que en la ciudad de Trujillo hay grandes botaderos de concretos los cuales no son reusados por el desconocimiento de los parámetros de estos materiales. En cuanto a los resultados de esta investigación se encontró porcentaje ideal de reemplazo es de 30% de agregado reciclado, además se determinó que las propiedades de este concreto (resistencia a la compresión), varían de 283.79 kg/cm2 a 281.74 kg/cm2 lo cual implica una reducción de menos del 5% con respecto al concreto tradicional (probeta patrón 0%).

The present investigation was carried out at Private University of Trujillo, the compressive strength of recycled concrete samples with controlled parameters was determined. This research explains the influence of the percentage and maximum nominal size of recycled concrete as a substituent of the coarse aggregate, on the compressive strength of a recycled concrete; based on a Type I portland cement. The percentages of recycled concrete added were 0%, 10%, 20%, 30%, 40% and 50%, for maximum nominal sizes of the coarse aggregate, and using a water / cement ratio of 0.56 with a design resistance of 210 kg / cm3. The mix design was elaborated based on the characterization of the concrete materials according to method ACI 211, in fresh condition for the concrete: the unit weight test was carried out according to ASTM C 138, concrete density (expressed in kg / cm3 ), then 36 test pieces (15 cm in diameter and 30 cm in height) were prepared and subjected to curing by immersion in water for 28 days according to ASTM C 31, then in hardened state for the recycled concrete: the test was carried out compressive strength according to ASTM C 39 for the determination of the load that will support this concrete (expressed in kg / cm2), the problem is that in the city of Trujillo there are large dumps of concrete which are not reused due to the ignorance of the parameters of these materials. Regarding the results of this research, it was found that 30% recycled concrete can be used, and it was determined that the properties of this concrete are from 283.79 kg/cm2 to 281.74 kg/cm2 which implies a reduction of less 5% with respect to traditional concrete (standard test tube 0%).
Disciplina académico-profesional: Ingeniería Civil
Institución que otorga el grado o título: Universidad Privada de Trujillo. Facultad de Ingeniería
Grado o título: Ingeniero Civil
Fecha de registro: 10-jul-2020

Ficheros en este ítem:
Fichero Tamaño Formato  
TESIS - VEGAS QUIROZ - CRUZ CALAPUJA.pdf
  Acceso restringido
2.35 MBAdobe PDFVisualizar/Abrir  Solicita una copia


Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons Creative Commons