Título: Comparación de la capacidad remineralizadora y la resistencia a la desmineralización del esmalte dental expuesto a 3 tipos de fluoruros. Estudio in vitro
Asesor(es): Delgado Cotrina, Leyla Antoinette; Ccahuana Vasquez, Renzo Alberto
Campo OCDE: http://purl.org/pe-repo/ocde/ford#3.01.05; http://purl.org/pe-repo/ocde/ford#3.01.06; http://purl.org/pe-repo/ocde/ford#3.02.14
Fecha de publicación: 2018
Institución: Universidad Peruana Cayetano Heredia
Resumen: Objetivo: Comparar la capacidad remineralizadora y la resistencia a la desmineralización del esmalte dental luego de ser expuesta a tres tipos de Fluoruros. Materiales y Métodos: Se utilizaron 64 bloques de esmalte dental humano (4x4x3mm) distribuidos aleatoriamente en 4 grupos según el agente fluorado: G1: Fluoruro de Amina gel 1.25% F, G2: Fluoruro Estañoso gel 0.4% F, G3: Fluoruro de Sodio gel 2% y un grupo control con saliva artificial. Cada muestra se expuso por 3 min al Fluoruro determinado y después sometidas al proceso de Desmineralización/Remineralización (Des/Re), siendo sumergidas 3h en solución desmineralizante seguido por 21 h en solución remineralizante durante 10 días. Se evaluó la microdureza Vickers antes y después de la exposición al Fluoruro, como también después del proceso Des/Re. Resultados: Las muestras que fueron expuestas al Fluoruro de sodio presentaron mayores valores de microdureza que los otros grupos. Luego del ciclo Des/Re los grupos del Fluoruro de amina y estañoso presentaron mayores valores que los otros grupos. Conclusión: Se encontró que el Fluoruro de sodio presentó mayor capacidad remineralizadora, mientras que el Fluoruro estañoso y el Fluoruro de amina proporcionan mayor resistencia a la desmineralización luego del ciclo Des/Re.

Objective: To compare the capacity of remineralization and demineralization resistance of human dental enamel after being exposed to three types of fluorides. Materials and methods: 64 blocks of human dental enamel (4x4x3mm) were randomly distributed into 4 groups according to the fluoridated agent: G1: Amine Fluoride gel (1.25% F), G2: Stannous Fluoride gel (0.4% F), G3: Sodium Fluoride gel (2% F) and a group control with artificial Saliva. Each sample was exposed for 3 min to the specific treatment group and then exposed to an in vitro cycling process of demineralization/remineralization (Des/Re), submerged 3 h in demineralizing solution followed by 21 h in remineralizing solution, during 10 days. Vickers microhardness was evaluated before and after exposure to the treatments, and also after the Des/Re process. Results: The Sodium Fluoride group showed higher values of microhardness than the other groups after the Fluoride exposure, amine and stannous Fluoride groups showed than the others. Conclusions: The Sodium Fluoride group showed greater remineralization ability, while the Stannous Fluoride and the Amine Fluoride showed better resistance to demineralization after the Des/Re cycling.
Disciplina académico-profesional: Estomatología
Institución que otorga el grado o título: Universidad Peruana Cayetano Heredia. Escuela de Posgrado Víctor Alzamora Castro
Grado o título: Maestro en Estomatología
Jurado: Más Lopez, Janett; Ramos Portocarrero, Oswaldo; Webb Linares, Louise Jacqueline
Fecha de registro: 23-sep-2024



Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons Creative Commons