Título: Diseño de concreto F`C 140 Kg/cm2 a base de concreto cascote con cemento Portland Tipo I - Trujillo
Asesor(es): Medina Carbajal, Lucio Sigifredo
Palabras clave: ConcretoDiseño de Mezcla
Campo OCDE: https://purl.org/pe-repo/ocde/ford#2.01.00
Fecha de publicación: 2024
Institución: Universidad Privada Antenor Orrego
Resumen: Se ha determinado el diseño de la sustitución del concreto normal por el concreto con cascote, en la propiedad mecánica del concreto utilizando cemento portland tipo I. Para lo cual; se tomaron dos diseños de mezclas con relación a/c (0.68) y con un asentamiento de 3”. Se elaboró y curo 25 probetas cilíndricas para cada relación a/c en concordancia a la Norma ASTM C 192 y ASTM C 39. Así mismo se tomó en cuenta los resultados de ensayos con las edades de 7, 14 y 28 días respectivamente. Se realizó el diseño de mezcla para una resistencia a la compresión de f`c 140 kg/cm2; con diseño de mezclas con concreto normal y con concreto de cascote producto de la demolición de vivienda en la zona de Trujillo, conservando la misma relación a/c de 0.68 para ambos diseños; teniendo un valor constante en la cantidad de agregados que se utilizó para el ensayo realizado, así mismo logró determinar que para ambos diseños de mezclas con concreto normal y concreto de cascote en la edad de 7 días (el concreto normal tiene un porcentaje de resistencia a la compresión de 70% a comparación del concreto de cascote se obtuvo 78%), en la edad de 14 días (el concreto normal tiene un porcentaje de resistencia a la compresión de 85% a comparación del concreto de cascote se obtuvo 85%) y finalmente a los 28 días de curado el concreto normal tiene un porcentaje de resistencia a la compresión de 115% a comparación del concreto de cascote se obtuvo 116%. Cabe recalcar que se observó que la Resistencia según las edades antes mencionadas no perjudican a la Resistencia patrón que es de F`C 140 kg/cm2

The design of the replacement of normal concrete with concrete with rubble has been determined, based on the mechanical property of the concrete using type I Portland cement. For which; Two mix designs were taken with w/c ratio (0.68) and with a slump of 3”. 25 cylindrical specimens were prepared and cured for each w/c ratio in accordance with ASTM C 192 and ASTM C 39. These results in their tests are ages of 7, 14 and 28 days respectively. The mix design was carried out for a compressive strength of f`c 140 kg/cm2; with mixture design with normal concrete and with rubble concrete resulting from the demolition of housing in the Trujillo area, maintaining the same w/c ratio of 0.68 for both designs; having a constant value in the amount of aggregates that was used for the test carried out, it was also possible to determine that for both mixture designs with normal concrete and rubble concrete at the age of 7 days (normal concrete has a compressive strength percentage of 70% compared to rubble concrete, 78% was obtained), at the age of 14 days (normal concrete has a compressive strength percentage of 85%, compared to rubble concrete, 85% was obtained) and finally after 28 days of curing, normal concrete has a compressive strength percentage of 115%, compared to rubble concrete, 116% was obtained. It should be noted that it was observed that the Resistance according to the aforementioned ages does not harm the standard Resistance, which is F`C 140 kg/cm2
Disciplina académico-profesional: Ingenieria Civil
Institución que otorga el grado o título: Universidad Privada Antenor Orrego. Facultad de Ingenieria
Grado o título: Ingeniero Civil
Jurado: Hurtado Zamora, Oswaldo; Velásquez Diaz, Gilberto Anaximandro; Perrigo Sarmiento, Felix Gilberto
Fecha de registro: 19-ago-2024



Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons Creative Commons