Aldazábal, O., (2015). Evaluación de la estabilidad dimensional de los diferentes tipos de ceras para registro interoclusal [Tesis, Universidad Nacional Mayor de San Marcos]. https://hdl.handle.net/20.500.12672/4382
Aldazábal, O., Evaluación de la estabilidad dimensional de los diferentes tipos de ceras para registro interoclusal [Tesis]. PE: Universidad Nacional Mayor de San Marcos; 2015. https://hdl.handle.net/20.500.12672/4382
@misc{renati/491705,
title = "Evaluación de la estabilidad dimensional de los diferentes tipos de ceras para registro interoclusal",
author = "Aldazábal Orué, Oscar Roberto",
publisher = "Universidad Nacional Mayor de San Marcos",
year = "2015"
}
--- This experimental study was conducted to evaluate and compare the dimensional stability of the wax interocclusal record Aluwax, Cavex Up and Koriwax at different times, these materials commonly used in dental schools for the centric or eccentric jaw relations before and during the dental treatment. A custom made metal apparatus with upper and lower members simulating maxillary and mandibular prepared was fabrited. 30 interocclusal records in each of the waxes, underwent these procedures specified by the manufacturer prior to registration were prepared. Weighing one kg on the apparatus to simulate the force exerted during registration. Vertical differences were measured with manual micrometer, records were measured after 10 sec, 1 hour, 24 hours and 48 hours, Its were at room temperature. For statistical was used analysis t-Student's. The results showed variations of up to 1mm in Aluwax waxes on steep surfaces and concave surfaces 0.1 mm, while Koriwax, Cavex and had similar values for both types of surfaces 0.2 ± 0.5mm, within 24 hours. It was concluded that the differences are of clinical interest in both types of surfaces and in all three types of wax interocclusal record, showing greater variation in the Aluwax steep surfaces wax and wax Cavex concave surfaces Keywords: Dimensional stability, Registration waxes, waxes pattern, wax printing