Citas bibligráficas
Esta es una referencia generada automáticamente. Modifíquela de ser necesario
Radunovic, X., Peña, F. (2024). Plan de marketing para Alta Comunicación [Trabajo de suficiencia profesional, Universidad Peruana de Ciencias Aplicadas (UPC)]. http://hdl.handle.net/10757/674415
Radunovic, X., Peña, F. Plan de marketing para Alta Comunicación [Trabajo de suficiencia profesional]. PE: Universidad Peruana de Ciencias Aplicadas (UPC); 2024. http://hdl.handle.net/10757/674415
@misc{renati/418935,
title = "Plan de marketing para Alta Comunicación",
author = "Peña Riofrio, Fiorella Alessandra",
publisher = "Universidad Peruana de Ciencias Aplicadas (UPC)",
year = "2024"
}
Título: Plan de marketing para Alta Comunicación
Otros títulos: Improvement of the compressive and flexural stress of concrete f´c=280kg/cm2 with the addition of recycled galvanized steel fibers, for application in pavements, in Metropolitan Lima
Asesor(es): Escala Pasco, Enzo
Palabras clave: Concreto; Fibra de Acero; Esfuerzo de Compresión; Esfuerzo de Flexión; Esfuerzo Residual; Concrete; Steel Fiber; Compression Stress; Flexure Stress; Residual Stress
Campo OCDE: https://purl.org/pe-repo/ocde/ford#5.08.00; https://purl.org/pe-repo/ocde/ford#5.00.00
Fecha de publicación: 10-jul-2024
Institución: Universidad Peruana de Ciencias Aplicadas (UPC)
Resumen: Actualmente existen problemas de fisuración y bajo esfuerzo residual de pavimentos rígidos en zonas comerciales. El presente proyecto busca combinar el aporte de las propiedades mecánicas de las fibras recicladas provenientes de perfiles de drywall en desuso con el concreto con el objetivo de mejorar los esfuerzos a flexión y esfuerzo residual sin afectar los esfuerzos a compresión de pavimentos rígidos enfocados en zonas comerciales que presentan problemas de fisuración.
Se ensayarán probetas prismáticas y cilíndricas con dosificaciones de 0.5%, 1% y 1.5% con respecto al peso del concreto. Respecto del esfuerzo residual máximo con dosificaciones de 1.5% de adición de fibras para deflexiones de 3 mm se obtuvo un valor 3.69 MPa. El esfuerzo máximo obtenido se encuentra en el orden de 5.20 MPa a 5.34 MPa. La resistencia a la compresión incrementó con adiciones de 1.5% de fibra alcanzando los 383.02 kg/cm2. Por el contrario, la trabajabilidad disminuyó considerablemente, hasta un 36% para adiciones de 1.5%, obteniéndose slump de 1 ½”.
De acuerdo con el análisis de los resultados obtenidos se puede concluir que la resistencia residual del concreto con adiciones de fibra de acero reciclado para proporciones de 0.5% a 1.5 % se incrementa, así como también la resistencia a la flexión y compresión. Por lo que su aplicación en elementos horizontales como losas es factible al encontrarse justificada su capacidad estructural de acuerdo con la normativa española y con fibras producto de algunas investigaciones citadas en el presente documento.
Currently, there are issues with cracking and low residual effort in rigid pavements in commercial areas. This project aims to combine the mechanical properties of recycled fibers from unused drywall profiles with concrete to improve flexural strength and residual effort without affecting the compressive strength of rigid pavements, focusing on commercial areas that have cracking problems. Prismatic and cylindrical specimens will be tested with dosages of 0.5%, 1%, and 1.5% relative to the weight of the concrete. Regarding the maximum residual effort with dosages of 1.5% fiber addition for deflections of 3 mm, a value of 3.69 MPa was obtained. The maximum effort obtained is in the range of 5.20 MPa to 5.34 MPa. The compressive strength increased with additions of 1.5% fiber, reaching 383.02 kg/cm². On the other hand, workability decreased significantly, by up to 36% for additions of 1.5%, resulting in a slump of 1 ½”. According to the analysis of the results obtained, it can be concluded that the residual strength of concrete with recycled steel fiber additions for proportions of 0.5% to 1.5% increases, as well as the flexural and compressive strength. Therefore, its application in horizontal elements such as slabs is feasible since its structural capacity is justified in accordance with Spanish regulations and with fibers resulting from some research cited in this document.
Currently, there are issues with cracking and low residual effort in rigid pavements in commercial areas. This project aims to combine the mechanical properties of recycled fibers from unused drywall profiles with concrete to improve flexural strength and residual effort without affecting the compressive strength of rigid pavements, focusing on commercial areas that have cracking problems. Prismatic and cylindrical specimens will be tested with dosages of 0.5%, 1%, and 1.5% relative to the weight of the concrete. Regarding the maximum residual effort with dosages of 1.5% fiber addition for deflections of 3 mm, a value of 3.69 MPa was obtained. The maximum effort obtained is in the range of 5.20 MPa to 5.34 MPa. The compressive strength increased with additions of 1.5% fiber, reaching 383.02 kg/cm². On the other hand, workability decreased significantly, by up to 36% for additions of 1.5%, resulting in a slump of 1 ½”. According to the analysis of the results obtained, it can be concluded that the residual strength of concrete with recycled steel fiber additions for proportions of 0.5% to 1.5% increases, as well as the flexural and compressive strength. Therefore, its application in horizontal elements such as slabs is feasible since its structural capacity is justified in accordance with Spanish regulations and with fibers resulting from some research cited in this document.
Enlace al repositorio: http://hdl.handle.net/10757/674415
Disciplina académico-profesional: Comunicación y Marketing
Institución que otorga el grado o título: Universidad Peruana de Ciencias Aplicadas (UPC). Facultad de Comunicaciones
Grado o título: Licenciado en Comunicación y Marketing
Jurado: Alarcón Chumbes, Medalit Elcina; Lozano Grández, Jorge Alfredo
Fecha de registro: 31-jul-2024
Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons