Título: Análisis y evaluación de las propiedades mecánicas de un muro de albañilería elaborado a base de tereftalato de polietileno, poliestireno expandido y cemento portland tipo I , a escala 1/25 de acuerdo a la norma técnica peruana
Asesor(es): Galicia Guarniz, William Conrad
Palabras clave: MecánicasTécnica
Campo OCDE: http://purl.org/pe-repo/ocde/ford#2.01.00
Fecha de publicación: 2021
Institución: Universidad Privada Antenor Orrego
Resumen: Esta investigación tuvo como objetivo principal determinar los resultados de reutilizar los residuos de plástico: Tereftalato de Polietileno y Poliestireno, como refuerzo en la elaboración de concreto ecológico para la construcción de elementos no estructurales. Analizar y establecer la mejora de las propiedades mecánicas de un ladrillo agregando Tereftalato de polietileno y Poliestireno expandido en su fabricación, definidas en la norma técnica E.070, para lo cual se fabricaron 1600 ladrillos en escala 1:25 del tamaño real, los cuales fueron confeccionados y elaborados con 15 kg de Cemento Portland Tipo I, 2 plancha de Polietileno Expandido (Tecnopor) y 5 Botellas de Tereftalato de polietileno (PET). Luego de la elaboración de estas muestras, se elaboraron 40 pequeños muros con las unidades de albañilería en la escala mencionada, en donde para el mortero se consideró 1 kg de cemento, posteriormente se analizó su grado de absorción, el índice de vacíos de los mismos, se realizó a su vez el ensayo de compresión diagonal de los muros mediante una carga cíclica. Se concluyó que las propiedades mecánicas de los ladrillos de concreto al adicionar Tereftalato de polietileno y Polietileno Expandido reciclado no mejoran, habiendo una disminución máxima de la resistencia a compresión del ladrillo de 59.84 kg/cm2 o 34.8%, respecto de la mezcla patrón; sin embargo, las propiedades físico mecánicas de los tres tipos de ladrillo de concreto con plástico PET reciclado alcanzando así cumplir con El Reglamento Nacional de Edificaciones E-0.70

The main objective of this research was to determine the results of reusing plastic waste: Polyethylene Terephthalate and Polystyrene, as a reinforcement in the elaboration of ecological concrete for the construction of non-structural elements. Analyze and establish the improvement of the mechanical properties of a brick by adding polyethylene terephthalate and expanded polystyrene in its manufacture, defined in the technical standard E.070, for which 1600 bricks were manufactured in 1:25 scale of the real size, which They were made and made with 15 kg of Type I Portland Cement, 2 Expanded Polyethylene (Tecnopor) plates and 5 Polyethylene Terephthalate (PET) bottles. After the elaboration of these samples, 40 small walls were elaborated with the masonry units in the mentioned scale, where for the mortar 1 kg of cement was considered, later its absorption degree, the void index of the same were analyzed. In turn, the diagonal compression test of the walls was carried out by means of a cyclical load. It was concluded that the mechanical properties of concrete bricks when adding polyethylene Terephthalate and recycled Expanded Polyethylene do not improve, having a maximum decrease in the compressive strength of the brick of 59.84 kg / cm2 or 34.8%, with respect to the standard mixture; However, the physical-mechanical properties of the three types of concrete brick with recycled PET plastic, thus complying with the National Building Regulation E-0.70
Disciplina académico-profesional: Ingeniería Civil
Institución que otorga el grado o título: Universidad Privada Antenor Orrego. Facultad de Ingeniería
Grado o título: Ingeniero Civil
Jurado: Cancino Rodas, Cesar Leónidas; Urteaga García, Juan Manuel; Luján Silva, Enrique Francisco
Fecha de registro: 14-jun-2021



Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons Creative Commons