Título: Influencia del superplastificante chema plast en el asentamiento y resistencia a la compresión del concreto cemento-arena elaborado solamente con agregado fino, Iquitos- 2022
Asesor(es): Ríos Vargas, Caleb
Campo OCDE: https://purl.org/pe-repo/ocde/ford#2.01.00
Fecha de publicación: 6-ene-2023
Institución: Universidad Científica del Perú
Resumen: En esta investigación de nivel descriptivo y diseño no experimental, se examina los efectos del aditivo mejorador de trabajabilidad del concreto y reductor de agua “Plastificante Chema Plast”, en el peso unitario y asentamiento del concreto cemento – arena en estado fresco, y en las propiedades de resistencia a la compresión, flexión, tracción, módulo de elasticidad y módulo de poisson. Se utilizaron tres tres relaciones agua/cemento: 0.55, 0.65 y 0.75; asimismo, correspondientemente se utilizó 9.19 lt/m3, 7.70 lt/m3 y 6.91 lt/m3 de aditivo chema plast; el cemento usado fue APU tipo GU y arena de 1.40 de módulo de fineza y superficie especifica de 69.735. Los resultados encontrados indican que la relación A/C de 0.55 incrementó el slump en 1/8” frente a los 3/8” de la relación 0.75. Sin embargo, la resistencia a la compresión a los 28 días de curado se incrementó de 285 kg/cm2 a 287 kg/cm2, de 171 kg/cm2 a 192 kg/cm2 y de 144 kg/cm2 a 159 kg/cm2, respectivamente. En las otras propiedades no existió variación significativa, pero si se pudo concluir que siendo mínimo el incremento de los valores de trabajabilidad y resistencia, no existe eficacia del uso del aditivo chema plast en la elaboración del concreto cemento – arena.

In this descriptive level investigation and non-experimental design, the effects of the concrete workability improving and water reducing additive “Chema Plast Plasticizer” are examined on the unit weight and settlement of cement-sand concrete in the fresh state, and on the properties of compressive strength, bending, tensile, modulus of elasticity and Poisson's modulus. Three water/cement ratios were used: 0.55, 0.65 and 0.75; Likewise, 9.19 lt/m3, 7.70 lt/m3 and 6.91 lt/m3 of chema plast additive were used correspondingly; The cement used was APU type GU and sand with a fineness modulus of 1.40 and a specific surface area of 69.735. The results found indicate that the A/C ratio of 0.55 increased the slump by 1/8” compared to 3/8” for the 0.75 ratio. However, the compressive strength at 28 days of curing increased from 285 kg/cm2 to 287 kg/cm2, from 171 kg/cm2 to 192 kg/cm2 and from 144 kg/cm2 to 159 kg/cm2, respectively. In the other properties there was no significant variation, but it could be concluded that the increase in workability and resistance values being minimal, there is no effectiveness in the use of the chema plast additive in the preparation of cement-sand concrete.
Disciplina académico-profesional: Ingeniería Civil
Institución que otorga el grado o título: Universidad Científica del Perú. Facultad de Ciencias e Ingeniería
Grado o título: Ingeniero Civil
Jurado: Irigoin Cabrera, Octavio Ulises; Ocaña Aponte, Juan Jesús; Arévalo Flores, Jefree Stefano
Fecha de registro: 23-abr-2024



Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons Creative Commons