Title: Evaluación comparativa de las propiedades físico - mecánicas y de conductividad térmica entre placas de fibrocemento y placas de fibrocemento adicionado con fibras de envases tetrabrik, fibras de aluminio y fibras de polietileno en el mes de diciembre en la ciudad del Cusco
Advisor(s): Soto Florez, Heiner
OCDE field: https://purl.org/pe-repo/ocde/ford#2.01.01
Issue Date: 10-Jun-2021
Institution: Universidad Andina del Cusco
Abstract: El fibrocemento está teniendo un protagonismo muy creciente a nivel constructivo dentro del sistema drywall utilizándose para: techos, tabiquería y revestimientos por su alta durabilidad, aislamiento térmico y fácil instalación, está conformado principalmente por cemento y fibras de origen vegetal. En la presente tesis se planteó la adición de fibras de envases tetrabrik, fibras de aluminio y fibras de polietileno en la elaboración de placas de fibrocemento, evaluando su comportamiento y resistencia y reduciendo el uso de la celulosa en este tipo de materiales, las fibras fueron obtenidas por procesos mecánicos. Se elaboraron tres placas de fibrocemento, se le añadió el 8 por ciento de fibras por total de mezcla a cada placa, se visualizó que las tres placas elaboradas presentaron un fraguado de 24 horas. Con las placas de fibrocemento fabricadas por mi persona se procedió a realizar una evaluación de las propiedades físicas y mecánicas empleando la norma alemana DIN y la norma americana ASTM, las pruebas a las que se sometieron las muestras fueron de: • Resistencia a la flexión • Compresión del espesor • Conductividad térmica Finalmente se realizó una comparativa de los ensayos entre probetas preparadas únicamente con fibrocemento y las probetas de fibrocemento adicionado con fibras de tetrabrik, aluminio y polietileno los resultados obtenidos fueron favorables, contribuyendo con el desarrollo de un nuevo material con un potencial de uso, exceptuando los de resistencia a flexión los cuales tuvieron un bajo rendimiento, y no cumpliendo los parámetros de la normativa DIN.

The asbestos cement is having a very increasing level constructive prominence inside the system drywall being used for: Roofs, tabiquería and coatings for their high durability, thermal insulation and easy installation, is shaped principally by cement and fibers of vegetal origin. In the present thesis the addition of fibers of containers proposed tetrabrik, fibers of aluminum and polyethylene fibers in the elaboration of plates of asbestos cement, evaluating your behavior and resistance and cutting down on the cellulose in this type of materials, fibers were gotten by mechanical processes. They elaborated three asbestos cement plates, it added to 8 percent of fibers for total from mixture each plate, that the three elaborate plates presented a 24-hour setting visualized itself. With the plates of asbestos cement manufactured by my person it was proceeded to accomplish an evaluation of the physical properties and mechanics using the German standard DIN and the American standard ASTM, the proofs you show them the ones they submitted to they were of: • Bending strength • Compression of thickness • Thermal conductivity Finally came true a comparison of the essays between test tubes prepared only with asbestos cement and the test tubes of asbestos cement added with fibers of tetrabrik, aluminum and polyethylene the obtained results were favorable, contributing with the development of a new material with a potential of use, excepting the ones of resistance to push-up which they had a low performance, and not keeping the normative DIN'S parameters.
Discipline: Ingeniería Civil
Grade or title grantor: Universidad Andina del Cusco. Facultad de Ingeniería y Arquitectura
Grade or title: Ingeniero Civil
Juror: Olazaval Rodríguez, María Milagros; Mendoza Escalante, Camilo; Calderón Gonzales, Werner Alfonso; Arbulu Jurado, Cesar Edilberto
Register date: 26-Oct-2021



This item is licensed under a Creative Commons License Creative Commons