Acosta, M. B., & Rodriguez, A. E. (2024). Influencia de la adición de plástico PET reciclado en la densidad, absorción y resistencia a la compresión en bloques de concreto para uso estructural, Trujillo 2023 [Tesis de licenciatura, Universidad Privada del Norte]. Repositorio de la Universidad Privada del Norte. https://hdl.handle.net/11537/39629 (es_PE)
. (es_PE)
https://hdl.handle.net/11537/39629
El plástico es uno de los principales contaminantes ambientales, es por ello que esta investigación tuvo como objetivo determinar la influencia de la adición de plástico reciclado PET en la densidad, absorción y resistencia a la comprensión en bloques de concreto para uso estructural, teniendo como diseño el método experimental. Para la elaboración de los bloques se tuvo como base una muestra patrón a la que se le adicionó el 5%, 10% y 15% de plástico PET los cuales fueron sometidos a ensayos establecidos por la NTP 399.602, 2017; los cuales fueron, resistencia a la compresión, densidad seca y absorción máxima. Los resultados obtenidos de los diseños de los bloques de concreto con adición de plástico PET reciclado al 5%, 10% y 15% en la resistencia a la compresión fueron de 15.51, 13.57 y 12.57 Mpa, para el ensayo a la absorción se obtuvo como resultado 73,80 y 84 kg/m3, mientras que en la densidad máxima se obtuvo como resultado 2074, 2050 y 1989 kg/ m3 respectivamente. Concluyendo que al adicionar 5% de plástico PET se cumple con los requisitos mínimos establecidos por la normativa. (es_PE)
Plastic is one of the main environmental pollutants, which is why this research aimed to determine the influence of the addition of recycled PET plastic on the density, absorption and resistance to compression in concrete blocks for structural use, having as a design the experimental method. To prepare the blocks, a standard sample was used as a base to which 5%, 10% and 15% of PET plastic was added, which were subjected to tests established by NTP 399.602, 2017; which were, compressive strength, dry density and maximum absorption. The results obtained from the designs of the concrete blocks with the addition of recycled PET plastic at 5%, 10% and 15% in the compression resistance were 15.51, 13.57 and 12.57 Mpa, for the absorption test it was obtained as result 73.80 and 84 kg/m3, while at the maximum density the result was 2074, 2050 and 1989 kg/m3 respectively. Concluding that by adding 5% PET plastic the minimum requirements established by the regulations are met. (es_PE)
Tesis (es_PE)
application/pdf (es_PE)
application/msword (es_PE)
spa (es_PE)
Universidad Privada del Norte (es_PE)
info:eu-repo/semantics/openAccess (es_PE)
https://creativecommons.org/licenses/by-nc-nd/3.0/us/ (*)
Universidad Privada del Norte (es_PE)
Repositorio Institucional - UPN (es_PE)
Concreto (es_PE)
Resistencia a la compresión (es_PE)
Hormigón -- Aditivos (es_PE)
Plásticos (es_PE)
Concrete block (es_PE)
PET plastic (es_PE)
Compression resistance (es_PE)
Influencia de la adición de plástico PET reciclado en la densidad, absorción y resistencia a la compresión en bloques de concreto para uso estructural, Trujillo 2023 (es_PE)
info:eu-repo/semantics/bachelorThesis (es_PE)
Universidad Privada del Norte. Facultad de Ingeniería (es_PE)
Ingeniería Civil (es_PE)
Título Profesional (es_PE)
Ingeniero Civil (es_PE)
PE (es_PE)
https://purl.org/pe-repo/ocde/ford#2.01.01 (es_PE)
Pregrado (es_PE)
https://purl.org/pe-repo/renati/level#tituloProfesional (es_PE)
71412783
https://orcid.org/0000-0002-8874-4885 (es_PE)
74248302
71025655
732016 (es_PE)
Rabanal Chavez, Erick Humberto
Jovanovic Aguirre, Jvan
Alvarado Ruiz, Cinthya Vanessa
https://purl.org/pe-repo/renati/type#tesis (es_PE)
Privada societaria



This item is licensed under a Creative Commons License Creative Commons