Mosqueira Moreno, Miguel Ángel
Daga Izquierdo, Carmen Rosmery
2022-07-22T10:50:07Z
2022-07-22T10:50:07Z
2022-03-14
Daga, C. R. (2022). Resistencia a compresión axial de ladrillos de arcilla incorporando ceniza de bagazo de caña de azúcar, Cajamarca 2019 [Tesis de licenciatura, Universidad Privada del Norte]. Repositorio de la Universidad Privada del Norte. https://hdl.handle.net/11537/30970 (es_PE)
620.1124 DAGA 2022 (es_PE)
https://hdl.handle.net/11537/30970
La investigación realizada tuvo por objetivo evaluar la resistencia a la compresión axial de unidades de albañilería incorporando ceniza de bagazo de caña de azúcar (CBCA). La muestra estuvo constituida por un total de 100 ladrillos, para lo cual se elaboraron 25 ladrillos para muestra patrón y 25 por cada porcentaje (3%, 5% y 7%). Se evaluaron las propiedades mecánicas y físicas de las muestras, mediante los ensayos de resistencia a la compresión, absorción y alabeo en el laboratorio de la Universidad Privada del Norte. Los resultados obtenidos fueron que las propiedades mecánicas en el ensayo de resistencia a la compresión, la unidad de albañilería sin incorporación de CBCA presenta mejor compresión axial (40.98 kg/cm), comparado con las unidades de albañilería con adición de CBCA al 3%, 5% y 7%, las que mostraron una resistencia de 31.80 kg/cm², 21.26 kg/cm² y 18.15 kg/cm², respectivamente. Asimismo, se obtuvo que en la propiedad física de absorción la unidad de albañilería con adición de CBCA al 7% presenta mayor absorción con respecto a las demás muestras; mientras que, en la propiedad física de alabeo, ninguna de las muestras excede a lo permitido por la Norma E-070. Se concluye que el uso CBCA en los diferentes porcentajes de 3 %, 5% y 7% en la elaboración de ladrillos de arcilla, no poseen mayor resistencia a las propiedades mecánicas y físicas, comparadas con el ladrillo de la muestra patrón. (es_PE)
The objective of the research carried out was to evaluate the resistance to axial compression of masonry units incorporating sugar cane bagasse ash (CBCA). The sample consisted of a total of 100 bricks, for which 25 bricks were made for the standard sample and 25 for each percentage (3%, 5% and 7%). The mechanical and physical properties of the samples were evaluated by means of resistance tests to compression, absorption and warping in the laboratory of the Universidad Privada del Norte. The results obtained were that the mechanical properties in the compressive strength test, the masonry unit without the incorporation of CBCA presents better axial compression (40.98 kg/cm), compared to the masonry units with the addition of CBCA at 3%, 5% and 7%, which showed a resistance of 31.80 kg/cm², 21.26 kg/cm² and 18.15 kg/cm², respectively. Likewise, it was obtained that in the physical property of absorption, the masonry unit with the addition of CBCA at 7% presents greater absorption with respect to the other samples; while, in the physical property of warping, none of the samples exceeds what is allowed by Standard E-070. It is concluded that the use of CBCA in the different percentages of 3%, 5% and 7% in the elaboration of clay bricks, do not have greater resistance to mechanical and physical properties, compared to the brick of the standard sample. (es_PE)
Tesis (es_PE)
application/pdf (es_PE)
application/msword (es_PE)
spa (es_PE)
Universidad Privada del Norte (es_PE)
info:eu-repo/semantics/embargoedAccess (es_PE)
Universidad Privada del Norte (es_PE)
Repositorio Institucional - UPN (es_PE)
Resistencia a la compresión (es_PE)
Materiales de construcción (es_PE)
Ladrillos (es_PE)
Arcilla (es_PE)
Ceniza de bagazo de caña de azúcar (es_PE)
Alabeo (es_PE)
Absorción (es_PE)
Resistencia a compresión axial de ladrillos de arcilla incorporando ceniza de bagazo de caña de azúcar, Cajamarca 2019 (es_PE)
info:eu-repo/semantics/bachelorThesis (es_PE)
Universidad Privada del Norte. Facultad de Ingeniería (es_PE)
Ingeniería Civil (es_PE)
Título Profesional (es_PE)
Ingeniero Civil (es_PE)
PE (es_PE)
https://purl.org/pe-repo/ocde/ford#2.01.01 (es_PE)
Pregrado (es_PE)
https://purl.org/pe-repo/renati/level#tituloProfesional (es_PE)
26733060
https://orcid.org/0000-0003-2668-4909 (es_PE)
42399203
732016 (es_PE)
Salazar Huamán, Erlyn Giordany
Carranza Liza, Mario Rene
Merma Gallardo, Lizbeth Milagros
http://purl.org/pe-repo/renati/type#tesis (es_PE)
Privada societaria



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.