Pacheco, G. A. (2016). Resistencia a compresión axial del concreto f’c=175 kg/cm2 incorporando diferentes porcentajes de viruta de acero ensayadas a diferentes edades, UPN - 2016 (Tesis de licenciatura). Repositorio de la Universidad Privada del Norte. Recuperado de https://hdl.handle.net/11537/10488 (es_PE)
624 PACH 2016 (es_PE)
https://hdl.handle.net/11537/10488
RESUMEN En la presente investigación determiné la influencia en la resistencia a compresión axial del concreto f’c = 175 kg/cm2 con la incorporación de diferentes porcentajes de viruta de acero. La metodología de la investigación consistió en preparar mezclas de concreto de resistencia de 175 kg/cm2 incorporando distintos porcentajes de viruta de acero (2%, 4% y 6%), para posteriormente ser ensayados a los 7,14 y 28 días. Los resultados al incorporar el 2% de viruta de acero se obtuvo una resistencia f’c = 190.79 kg/cm2 a los 28 días, a este porcentaje de incorporación corresponde un incremento de la resistencia a compresión del 9.02%; al incorporar el 4% de viruta de acero se obtuvo una resistencia f’c = 196.82 kg/cm2 a los 28 días, a este porcentaje de incorporación corresponde un incremento de la resistencia a compresión del 12.47% y al incorporar del 6% de viruta metálica se obtiene una resistencia f’c = 202.26 kg/cm2 a los 28 días, a este porcentaje de adición corresponde un incremento de la resistencia a compresión del 15.58%. Concluyendo que los resultados obtenidos nos indican que los concretos incorporados con viruta de acero presentan una resistencia mayor a las del concreto convencional ensayadas a los 7, 14 y 28 días. (es_PE)
ABSTRACT In the present investigation to determine the influence on the resistance to axial compression of concrete fc = 175 kg/cm2 with the addition of different percentages of steel wool. The research methodology was to prepare concrete mixes strength of 175 kg/cm2 chip incorporating different percentages of steel (2%, 4% and 6%) to subsequently test them for 7,14 and 28 days. The results by incorporating 2% of steel wool resistance f'c = 190.79 one kg/cm2 at 28 days was obtained, this percentage incorporation rate increased compressive strength of 9.02%; incorporating 4% of steel wool resistance f'c = 196.82 one kg/cm2 at 28 days was obtained, this percentage incorporation rate increased compressive strength of 12.47% and 6% by incorporating chip metal resistance f'c = 202.26 one kg/cm2 after 28 days, this corresponds addition rate increased compressive strength of 15.58% is obtained. Concluded that the results indicate that the concrete embedded with steel wool have a higher than that of conventional concrete tested at 7, 14 and 28 days resistance. (es_PE)
Tesis (es_PE)
application/pdf (es_PE)
application/msword (es_PE)
spa (es_PE)
Universidad Privada del Norte (es_PE)
info:eu-repo/semantics/openAccess (es_PE)
https://creativecommons.org/licenses/by-nc-sa/3.0/us/ (*)
Universidad Privada del Norte (es_PE)
Repositorio Institucional - UPN (es_PE)
Resistencia a la compresión (es_PE)
Materiales de construcción (es_PE)
Concreto (es_PE)
Resistencia a compresión axial del concreto f’c=175 kg/cm2 incorporando diferentes porcentajes de viruta de acero ensayadas a diferentes edades, UPN - 2016 (es_PE)
info:eu-repo/semantics/bachelorThesis (es_PE)
Universidad Privada del Norte. Facultad de Ingeniería (es_PE)
Ingeniería Civil (es_PE)
Título Profesional (es_PE)
Ingeniero Civil (es_PE)
PE (es_PE)
https://purl.org/pe-repo/ocde/ford#2.01.01 (es_PE)
Pregrado (es_PE)
https://purl.org/pe-repo/renati/level#tituloProfesional (es_PE)
40208212
40618377
732016 (es_PE)
Aguilar Aliaga, Orlando
Quispe Rodríguez, Gerson
Salazar Huamán, Erlyn Giordany
https://purl.org/pe-repo/renati/type#tesis (es_PE)
Privada societaria



This item is licensed under a Creative Commons License Creative Commons