Title: Los microorganismos eficaces EM-1 y su efecto en la resistencia a la compresión y flexión del concreto f’c=210 kg/cm²
Advisor(s): Farfán Córdova, Marlon Gastón
OCDE field: http://purl.org/pe-repo/ocde/ford#2.01.00
Issue Date: 2023
Institution: Universidad Privada Antenor Orrego
Abstract: Esta investigación se llevó a cabo para determinar el efecto de los microorganismos eficaces EM-1 en la resistencia a la compresión y flexión del concreto f’c=210 kg/cm2 , se reemplazó un porcentaje del agua por EM-1 según su diseño de mezcla. Se realizaron 120 especímenes de concreto, conformada por 4 mezclas: Concreto patrón (CP), Concreto con 2% de EM-1 (CP2EM), Concreto con 5% de EM-1 (CP5EM) y Concreto con 10% de EM-1 (CP10EM). De estos, 60 fueron probetas cilíndricas y 60 fueron probetas prismáticas, las cuales se sometieron a ensayos de comprensión y flexión respectivamente en los periodos de 7,14 y 28 días. Además, se aplicaron técnicas de caracterización como: Microscopio Electrónico de Barrido (MEB), Espectrometría de Rayos X de Energía Dispersiva (EDS) y Difracción de Rayos X (DRX), a fragmentos pertenecientes a las probetas. Los resultados mostraron que el concreto con 10% de EM-1 (CP10EM) tuvo mejor rendimiento a la resistencia a la compresión y flexión del concreto en 12.14% y 16.64% respectivamente con respecto al concreto patrón (CP). Las técnicas de caracterización realizadas a las muestras de concreto sugieren que la mejora de resistencia se debió debido a la segregación de carbonato de calcio (CaCO3) en la matriz de concreto

This research was carried out to determine the effect of effective microorganisms EM-1 on the compressive and flexural strength of concrete f'c=210 kg/cm2, a percentage of water was replaced by EM-1 according to its mix design. A total of 120 concrete specimens were made, consisting of 4 mixtures: Standard Concrete (CP), Concrete with 2% of EM-1 (CP2EM), Concrete with 5% of EM-1 (CP5EM) and Concrete with 10% of EM-1 (CP10EM). Of these, 60 were cylindrical specimens and 60 were prismatic specimens, which were subjected to compression and flexural tests respectively at 7, 14 and 28 days. In addition, characterization techniques such as Scanning Electron Microscopy (SEM), Energy Dispersive X-Ray Spectrometry (EDS) and X-Ray Diffraction (XRD) were applied to fragments belonging to the specimens. The results showed that the concrete with 10% EM-1 (CP10EM) performed better in compressive and flexural strength of the concrete by 12.14% and 16.64%, respectively, with respect to the standard concrete (CP). Characterization techniques performed on the concrete samples suggest that the strength improvement was due to the segregation of calcium carbonate (CaCO3) in the concrete matrix
Discipline: Ingeniería Civil
Grade or title grantor: Universidad Privada Antenor Orrego. Facultad de Ingeniería
Grade or title: Ingeniero Civil
Juror: Durand Orellana, Rocío del Pilar; Gálvez Paredes, José Alcides; Cancino Rodas, César Leonidas
Register date: 22-Nov-2023



This item is licensed under a Creative Commons License Creative Commons