Barzola Gastelú, Carlos Armando
Sáenz Correa, Elvis Emerson
Sáenz Correa, Elvis Emerson
2022-05-16T22:55:44Z
2022-05-16T22:55:44Z
2021
http://hdl.handle.net/20.500.14076/22081
El agua se ha vuelto un recurso escaso y la escasez del recurso hídrico ejerce presión sobre todas las actividades que realiza el ser humano. Actualmente se buscan fuentes alternativas para su uso que garanticen la sostenibilidad en el uso de este recurso vital. Esta tesis estudia el uso del agua residual tratada (ART) para la elaboración de concreto. Para el análisis de sus propiedades se desarrolló un diseño de mezcla de concreto patrón con agua potable y dos tipos de mezclas con calidades diferentes de agua. Para una de las mezclas se empleó agua residual tratada con tratamiento primario denominada ART-1. Para la otra mezcla se empleó agua residual tratada con tratamiento secundario denominada ART-2. Las aguas tratadas proceden de la Planta de Tratamiento de Aguas Residuales (PTAR) del Centro de Investigaciones de Tratamiento de Aguas Residuales y Residuos Peligrosos (CITRAR). En cada tipo de mezcla se emplearon relaciones agua/cemento de 0.70, 0.65 y 0.60. Se estudiaron los conceptos teóricos de los materiales usados en el diseño de mezcla y las propiedades del concreto. Con mayor ampliación se estudió sobre el agua residual tratada: definición, tecnologías, usos en el mundo, su aplicación en el diseño y elaboración de mezclas de concreto y su aplicación en el método del agregado global para el diseño de mezclas. Se realizaron ensayos de laboratorio para conocer las propiedades de los materiales usados. El diseño de mezclas priorizó la mejor combinación de los agregados, la cantidad de agua necesaria para obtener un concreto de consistencia adecuada (3”–4”) y lograr concretos de mediana a baja resistencia (relaciones agua/cemento de 0.70, 0.65 y 0.60). El concreto en estado fresco fue sometido a pruebas de asentamiento, fluidez, exudación, peso unitario, contenido de aire y tiempo de fraguado. Así mismo, el concreto en estado endurecido fue sometido a pruebas de compresión a los 7, 14, 28 y 42 días, ensayos de compresión diametral a los 28 días, ensayo de módulo elástico estático (M.E.E.), absorción, porcentaje de vacíos y densidad. Los resultados indican que los concretos elaborados con ART presentan mayor asentamiento con respecto al concreto patrón. Se aprecia una tendencia decreciente del asentamiento al disminuir la relación agua/cemento. No se presenta mucha variación en el peso unitario. El concreto con ART-1 presenta mayor fluidez y en el concreto con ART-2 es ligeramente menor. El concreto con ART-2 presenta mayor exudación y en el concreto con ART-1 es ligeramente superior. El concreto con ART-1 presenta mayor contenido de aire (hasta el doble) y en el concreto con ART-2 es ligeramente menor. El concreto con ART-1 presenta mayores incrementos en el tiempo de fraguado inicial (-12, +22 y +40 minutos) y en el concreto con ART-2 se presenta menores incrementos en el tiempo de fraguado inicial (-1, +16 y +17 minutos) cuando se disminuye la relación agua/cemento. El concreto con ART-1 presenta mayores incrementos en el tiempo de fraguado final (-10, +35 y +45 minutos) y en el concreto con ART-2 presenta menores incrementos en el tiempo de fraguado final (-5, -8 y +14 minutos) cuando se disminuye la relación agua/cemento. En ambos casos se tiene comportamientos ligeramente acelerantes y retardantes. Los ensayos en estado endurecido de los concretos con ART muestran disminución de la resistencia a la compresión en 20%, 13% y 10% (ART-1) y en 5%, 14% y 6% (ART-2) para las relaciones agua/cemento de 0.70, 0.65 y 0.60, respectivamente. La resistencia a la tracción disminuye en 23%, 12% y 8% (ART-1) y en 17%, 6% y 3% (ART-2) al disminuir la relación agua/cemento. El M.E.E. alcanzó 0%, -10% y -6% (ART-1) y +5%, -9% y -5% (ART-2) para las relaciones agua/cemento 0.70, 0.65 y 0.60, respectivamente. La absorción es mayor entre 2% y 15% y presenta una tendencia decreciente al disminuir la relación agua/cemento. La densidad es ligeramente menor y no presenta mucha variación con las diferentes relaciones agua/cemento. El porcentaje de vacíos es mayor, entre 1% y 11%, y presenta una tendencia decreciente al disminuir la relación agua/cemento. (es)
Water has become a scarce resource and the scarcity of water resources puts pressure on all the activities carried out by human beings. Alternative sources are currently being sought for its use that guarantee sustainability. This thesis studies the use of treated wastewater (ART from its Spanish initials) for making concrete. For the analysis of its properties, a design was developed for a standard concrete mix with drinking water and two types of mixes with wastewater. For one of the mixtures, wastewater treated with primary treatment called ART-1 was used. For the other mixture, wastewater treated with secondary treatment called ART-2 was used. The treated waters come from the Planta de Tratamiento de Aguas Residuales (PTAR) of the Centro the Investigaciones de Tratamiento de Aguas Residuals y Residuos Peligrosos (CITRAR). In each type of mix, water/cement ratios of 0.70, 0.65 and 0.60 were used. The theoretical background of the materials used in the mix design and the properties of concrete were studied. More extensively, the treatment of treated wastewater was studied: definition, technologies, uses in the world, its application in the design and elaboration of concrete mixes and its application in the global aggregate method for the design of concrete mixes. Laboratory tests were carried out to know the properties of the materials used. The design of mixtures prioritized the best combination of aggregates, the amount of water necessary to obtain a concrete of adequate consistency (3”–4”) and achieve concrete of medium to low strength (water/cement ratios of 0.70, 0.65 and 0.60). Fresh concrete was tested for settlement, fluidity, exudation, unit weight, air content and setting time. Likewise, hardened concrete was tested for compression strength at 7, 14, 28 and 42 days, diametral compression tests at 28 days, static elastic modulus (M.E.E. from its Spanish initials) test, absorption, void percentage and density. Results indicate that the concretes made with ART show higher settlement with respect to the standard concrete. A decreasing trend of settlement is observed as the water/cement ratio decreases. There is not much variation in unit weight. Concrete with ART-1 has higher fluidity and concrete with ART-2 it is slightly less. Concrete with ART-2 shows greater exudation and concrete with ART-1 is slightly higher. Concrete with ART-1 has higher air content (up to double) and in concrete with ART-2 it is slightly lower. Concrete with ART-1 shows greater increases in initial setting time (-12, +22 and +40 minutes) and concrete with ART-2 shows smaller increases in initial setting time (-1, +16 and +17 minutes) when the water/cement ratio is decreased. Concrete with ART-1 shows greater increases in final setting time (-10, +35 and +45 minutes) and concrete with ART-2 shows smaller increases in final setting time (-5, -8 and +14 minutes) when the water/cement ratio is decreased. In both cases there are slightly speeding and delaying effects. Tests results in the hardened state of the concretes with ART show a decrease in the compressive strength in 20%, 13% and 10% (ART-1) and in 5%, 14% and 6% (ART-2) for the water/cement ratios of 0.70, 0.65 and 0.60, respectively. The tensile strength decreases by 23%, 12% and 8% (ART-1) and by 17%, 6% and 3% (ART-2) as the water/cement ratio decreases. The M.E.E. reached 0%, -10% and -6% (ART-1) and + 5%, -9% and -5% (ART-2) for the water/cement ratios of 0.70, 0.65 and 0.60, respectively. The absorption is greater between 2% and 15% and presents a decreasing trend as the water/cement ratio decreases. The density is slightly lower and does not show much variation with the different water/cement ratios. The void percentage is higher, between 1% and 11%, and presents a decreasing trend as the water/cement ratio decreases. (en)
Tesis (es)
application/pdf (es)
spa (es)
Universidad Nacional de Ingeniería (es)
info:eu-repo/semantics/restrictedAccess (es)
http://creativecommons.org/licenses/by-nc-nd/4.0/ (es)
Universidad Nacional de Ingeniería (es)
Repositorio Institucional - UNI (es)
Concreto (es)
Propiedades del concreto (es)
Aguas residuales tratadas (es)
Análisis de las propiedades del concreto de mediana a baja resistencia elaborado con agua residual tratada (es)
info:eu-repo/semantics/bachelorThesis (es)
Universidad Nacional de Ingeniería. Facultad de Ingeniería Civil (es)
Ingeniería Civil (es)
Título Profesional (es)
Ingeniero Civil (es)
PE (es)
http://purl.org/pe-repo/ocde/ford#2.01.01 (es)
Ingeniería (es)
http://purl.org/pe-repo/renati/nivel#tituloProfesional (es)
10408631
https://orcid.org/0000-0002-6087-9702 (es)
46124810
732016
Quintana Alfaro, Noemi Leopoldina
Cachay Huamán, Rafael
http://purl.org/pe-repo/renati/type#tesis (es)
Pública



This item is licensed under a Creative Commons License Creative Commons