Torres-Romero, J. A. (2023).Diseño de un concreto 210 Kg/cm2 con piedra chancada e inclusión de fibra de vidrio y su influencia en la resistencia a la compresión en comparación con el concreto convencional. Tesis para optar el grado de Ingeniero Civil. Facultad de Ingeniería Civil y Arquitectura, Universidad Nacional de San Martín, Tarapoto, Perú. (es_PE)
http://hdl.handle.net/11458/5115
“Diseño de un concreto 210 Kg/cm2 con piedra chancada e inclusión de fibra de vidrio y su influencia en la resistencia a la compresión en comparación con el concreto convencional.” La investigación presentada tuvo como objetivo; buscar si la adición de fibra de vidrio en porcentajes de 1 %, 3 % y 5% aumenta la Resistencia del concreto. El ámbito de esta investigación es para todo el sistema del concreto donde se utiliza piedra chancada adicionando fibra de vidrio. El tiempo de la investigación fue de seis meses, y entre las teorías están los términos como las resistencias a flexión, compresión, diseño de mezcla, concreto, etc. Es una investigación no experimental de tipo explicativa y la población está basada en probetas adicionando fibra al 1%, 3% y 5%. La norma ASTM y la Norma ACI 109-02 permiten que la evaluación a estas probetas se realice de la siguiente manera: en volúmenes en relación a la arena, de acuerdo a esto se tiene como muestra 60 probetas y sin adición de fibra de vidrio en donde se realizaron ensayos de sus propiedades mecánicas, y cuya conclusión fue que con el uso de fibra de vidrio sí fue posible mejorar la resistencia del concreto en compresión. (es_PE)
"Design of a 210 Kg/cm2 concrete with crushed stone and inclusion of fiberglass and its influence on compressive strength compared to conventional concrete." The objective of the research presented was to find out if the addition of fiberglass in percentages of 1%, 3% and 5% increases the strength of concrete. The scope of this research is for the entire concrete system where crushed stone is used in addition to fiberglass. This research lasted six months, and among the theories are terms such as flexural strength, compressive strength, mix design, concrete, etc. It is a non-experimental research of explanatory type and the population is based on test tubes adding fiber at 1%, 3% and 5%. ASTM and ACI Standard 109-02 allow the evaluation of these test tubes to be carried out in the following way: in volumes in relation to the sand. According to this, 60 test tubes were sampled without the addition of fiberglass and their mechanical properties were tested, and the conclusion was that it was possible to improve the compressive strength of the concrete by using fiberglass. (es_PE)
application/pdf (es_PE)
spa (es_PE)
Universidad Nacional de San Martín. Fondo Editorial (es_PE)
info:eu-repo/semantics/openAccess (es_PE)
https://creativecommons.org/licenses/by/4.0/deed.es (es_PE)
Repositorio - UNSM (es_PE)
Concreto (es_PE)
Fibra de vidrio (es_PE)
Porcentaje (es_PE)
Resistencia a la compresión (es_PE)
Diseño de un concreto 210 Kg/cm2 con piedra chancada e inclusión de fibra de vidrio y su influencia en la resistencia a la compresión en comparación con el concreto convencional (es_PE)
info:eu-repo/semantics/bachelorThesis (es_PE)
Universidad Nacional de San Martín. Facultad de Ingeniería Civil y Arquitectura (es_PE)
Ingeniería Civil (es_PE)
Ingeniero Civil (es_PE)
PE (es_PE)
https://purl.org/pe-repo/ocde/ford#2.01.01 (es_PE)
https://purl.org/pe-repo/renati/nivel#tituloProfesional (es_PE)
https://orcid.org/0000-0003-3053-2908 (es_PE)
74253061
76558566
732016 (es_PE)
Rioja Diaz, Jorge Isaacs (es_PE)
Reategui Acedo, Ivan Gustavo (es_PE)
Sandoval Salazar, Nestor Raul (es_PE)
https://purl.org/pe-repo/renati/type#tesis (es_PE)
Pública
info:eu-repo/semantics/publishedVersion (es_PE)



Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons Creative Commons