Title: Evaluación comparativa de las propiedades físicas y mecánicas de morteros, adicionados con fibras de paca frente a un mortero tradicional
Advisor(s): Mamani Vargas, Elvis Yuri
OCDE field: https://purl.org/pe-repo/ocde/ford#2.01.01
Issue Date: 19-Dec-2023
Institution: Universidad Andina del Cusco
Abstract: El trabajo de investigación consistió en evaluar comparativamente las propiedades físicas y mecánicas de morteros adicionados con fibra de paca(Guadua weberbaueri Pilger) frente a un mortero tradicional se analizó las propiedades físicas y mecánicas mediante ensayos comparativos en estado fresco y endurecido, en el estado fresco se determinó en qué medida altera la fluidez del mortero y en qué medida se altera la fisuración en la contracción plástica del mortero y en el estado endurecido se determinó en qué medida varia la resistencia a la compresión y la resistencia a la flexión del mortero con la adición de fibras de paca en 300 g/m3; 600 g/m3 y 1000 g/m3 frente a un mortero tradicional. El diseño de mezcla se realizó utilizando los materiales como arena fina de Cunyac, cemento portland tipo IP, aditivo y fibra de paca en sus diferentes dosis en 300 g/m3; 600 g/m3 y 1000 g/m3 para lo cual se realizó 6 ensayos para cada dosis, 24 muestras para 7, 14 y 28 días que en total de muestras serian 72 muestras para resistencia a compresión y 72 muestras para resistencia a flexión, para el ensayo de contracción plástica un ensayo para cada dosis que hacen total de 4 muestras ensayadas. En la contracción plástica se pudo determinar que cuanta más fibra se incrementa el mortero más se reducen tanto la longitud como el ancho de la grieta y en la resistencia a la compresión y flexión, la adición de fibra es significativa si y solo si se acompaña el efecto del tiempo de curado. Finalmente, se concluyó que la dosis de fibra de paca en estado fresco afecta directamente y de forma significativa a la reducción tanto de la longitud como al ancho de las grietas formadas por retracción plástica del mortero, y en el mortero en estado endurecido no es significativa su resistencia a la compresión ni la resistencia a la flexión.

The research work consisted of comparatively evaluating the physical and mechanical properties of mortars added with bale fiber (Guadua weberbaueri Pilger) compared to a traditional mortar. The physical and mechanical properties were analyzed through comparative tests in the fresh and hardened state, in the fresh state. It was determined to what extent the fluidity of the mortar is altered and to what extent cracking is altered in the plastic contraction of the mortar and in the hardened state it was determined to what extent the compressive strength and flexural strength of the mortar vary with the addition of bale fibers at 300 g/m3; 600 g/m3 and 1000 g/m3 compared to a traditional mortar. The mix design was carried out using materials such as fine Cunyac sand, IP type Portland cement, additive and bale fiber in their different doses at 300 g/m3; 600 g/m3 and 1000 g/m3 for which 6 tests were carried out for each dose, 24 samples for 7, 14 and 28 days, which in total samples would be 72 samples for compression resistance and 72 samples for flexural resistance, for the plastic contraction test, one test for each dose, making a total of 4 samples tested. In plastic contraction it was determined that the more fiber the mortar increases, the more both the length and width of the crack are reduced and in the resistance to compression and flexion, the addition of fiber is significant if and only if it is accompanied by effect of curing time. Finally, it was concluded that the dose of bale fiber in the fresh state directly and significantly affects the reduction of both the length and width of the cracks formed by plastic shrinkage of the mortar, and in the mortar in the hardened state it is not significant. its compressive strength or flexural strength.
Note: Ciencia y Tecnología en el uso de Materiales
Discipline: Ingeniería Civil
Grade or title grantor: Universidad Andina del Cusco. Facultad de Ingeniería y Arquitectura
Grade or title: Ingeniero Civil
Juror: Somocurcio Alarcón, Hector Erick; Aguilar Hilari, Adan Renzo; Cana Paullo, Hugo; Alvarez Espinoza, Jorge
Register date: 7-May-2024; 7-May-2024



This item is licensed under a Creative Commons License Creative Commons