In this report the correlation between the index of maturity of concrete mixes and its compressive strength, made with portland cement type Ms and Ico is determined. We worked with a total of 84 samples of water cement ratios 0.54, 0.61 and 0.69, manufactured and cured in accordance with ASTM C 192 standard. With the help of a home electronic equipment, calibrated under standard ASTM C 1074. readings concrete temperature, at ages 1, 3, 7, 14, 21 and 28 days it was noted. Determining, at the same ages, the compressive strength using the ASTM F 39 standard. The maturity index is processed, according to the ASTM C1074 standard, using the equation of Nurse-Saul. Equations and degrees of correlation for Portland cement concrete with Ms: W / c ratio of 0.54: f’c = 49.885 ln (IM) - 229.84 and R2 = 0.9479 Kg/Cm2 W / c ratio of 0.61: f’c = 41.537 ln (IM) - 188.57 and R2 = 0.9476 Kg/Cm2 W / c ratio of 0.69: f’c = 32.558 ln (IM) - 145.42 and R2 = 0.9514 Kg/Cm2 For concrete with Portland cement type Ico: W / c ratio of 0.54: f’c = 51.149 ln (IM) - 234.60 and R2 = 0.9434 Kg/Cm2 W / c ratio of 0.61: f’c = 43.745 ln (IM) - 198.73 and R2 = 0.9456 Kg/Cm2 W / c ratio of 0.61: f’c = 34.628 ln (IM) - 155.92 and R2 = 0.9438 Kg/Cm2 (eng)
En el presente informe se determina la correlación entre el índice de madurez de mezclas de concreto y su resistencia a la compresión, fabricadas con cemento portland tipo Ms y Ico. Se trabajó con un total de 84 probetas de relaciones agua cemento 0.54, 0.61 y 0.69, fabricadas y curadas en concordancia a la norma ASTM C 192. Con la ayuda de un equipo electrónico casero, calibrado bajo la norma ASTM C 1074. Se tomó las lecturas de la temperatura del concreto, a las edades de 1, 3, 7, 14, 21 y 28 días. Determinando, a las mismas edades, la resistencia a la compresión aplicando la norma ASTM C 39. El índice de madurez se procesó, en concordancia a la norma ASTM C1074, mediante la ecuación de Nurse-Saúl. Las ecuaciones y grados de correlación para el concreto con cemento Portland tipo MS: Relación a/c de 0.54: f´c = 49.885 ln (IM) – 229.84 y R2= 0.9479 Kg/Cm2 Relación a/c de 0.61: f´c = 41.537 ln (IM) – 188.57 y R2= 0.9476 Kg/Cm2 Relación a/c de 0.69: f´c = 32.558 ln (IM) – 145.42 y R2= 0.9514 Kg/Cm2 Para el concreto con Cemento Portland tipo Ico: Relación a/c de 0.54: f´c = 51.149 ln (IM) – 234.60 y R2= 0.9434 Kg/Cm2 Relación a/c de 0.61: f´c = 43.745 ln (IM) – 198.73 y R2= 0.9456 Kg/Cm2 Relación a/c de 0.69: f´c = 34.628 ln (IM) – 155.92 y R2= 0.9438 Kg/Cm2 (spa)
Tesis (spa)
application/pdf (eng)
spa (spa)
Universidad Privada Antenor Orrego - UPAO (spa)
info:eu-repo/semantics/openAccess (eng)
Universidad Privada Antenor Orrego (spa)
Repositorio Institucional - UPAO (spa)
Índice de madurez (spa)
Mezcla de concreto (spa)
Resistencia de comprensión (spa)
Correlación entre el índice de madurez de una mezcla de concreto y su resistencia a la compresión (spa)
info:eu-repo/semantics/bachelorThesis (eng)
Universidad Privada Antenor Orrego. Facultad de Ingeniería (spa)
Ingeniería Civil (spa)
Título Profesional (spa)
Ingeniero Civil (spa)
Privada asociativa



IMPORTANTE
La información contenida en este registro es de entera responsabilidad de la universidad, institución o escuela de educación superior que administra el repositorio académico digital donde se encuentra el trabajo de investigación y/o proyecto, los cuales son conducentes a optar títulos profesionales y grados académicos. SUNEDU no se hace responsable por los contenidos accesibles a través del Registro Nacional de Trabajos de Investigación – RENATI.