El objetivo de la presente investigación fue evaluar el efecto in vitro del blanqueamiento con peróxido de hidrogeno al 35% y el peróxido de carbamida al 10% en la fuerza de adhesión de brackets. Se trabajó con un total de 33 premolares humanos dividiéndolos en 3 grupos aleatoriamente (n=11), en el Grupo I (control) no se aplicó blanqueamiento, en el Grupo II se aplicó blanqueamiento con peróxido de Hidrogeno al 35% y en el Grupo III se aplicó blanqueamiento con peróxido de Carbamida al 10%. Seguidamente, en todos los grupos se aplicó el ácido grabador (ácido fosfórico Densell® al 37%) por 15 segundos; las brackets fueron adheridas con Transbond XT® siguiendo las recomendaciones del fabricante, la resistencia al descementado fue realizada por el "INSTRON TESTING MACHINE" (2,00 mm/min). Los resultados fueron obtenidos en Newton (N) y transformados en Mega Pascales (MPa), tomando en cuenta la superficie del bracket (6mm2), y analizados con las pruebas ANOVA de un factor (p<=0.05) y el análisis estadístico de comparaciones múltiples HDS de Tukey y prueba t de Dunnett (bilateral). Los resultados indicaron que con la prueba ANOVA para un factor no existe diferencia estadísticamente significativa entre los grupos. Sin embargo, la prueba t de Dunnett, nos indicó que existe diferencia estadísticamente significativa entre el Grupo I (sin blanqueamiento) y el Grupo III (con blanqueamiento con PC-10%) reduciendo la fuerza de adhesión en 2.878 MPa. (spa)
The aim of this investigation was to evaluate the in vitro bleaching effect hydrogen peroxide and 35% carbamide peroxide 10% in the bond strength of brackets. We worked with a total of 33 human premolars randomly dividing them into 3 groups randomly (n = 11), In Group I (control) was applied whitening, In Group II Whitening Hydrogen peroxide 35% was applied, and Group III whitening carbamide peroxide was applied to 10%. Subsequently, all groups etchant (phosphoric acid 37% Densell ®) for 15 s was applied; the brackets were bonded with Transbond XT ® following the manufacturer's recommendations, debonding resistance was made by the "INSTRON TESTING MACHINE" (2.00 mm / min). The results were obtained in Newton (N) and transformed into Mega Pascals (MPa), taking into account the surface of the bracket (6mm2) and analyzed with ANOVA tests of a factor (p <= 0.05) and statistical analysis of comparisons multiple HDS Tukey and Dunnett t test (bilateral). The results indicated that the ANOVA test for a factor there is no statistically significant difference between groups. Dunnett's t-test indicates that there is a statistically significant difference between Group I (no bleaching) and Group III (with whitening PC-10%) in reducing 2,878 MPa. (eng)
Tesis (spa)
application/pdf (eng)
spa (spa)
Universidad Privada Antenor Orrego - UPAO (spa)
info:eu-repo/semantics/openAccess (eng)
Universidad Privada Antenor Orrego (spa)
Repositorio Institucional - UPAO (spa)
Fuerza de adhesión de brackets (spa)
Blanqueamiento (spa)
Brackets sobre dientes (spa)
Comparación in vitro de la fuerza de adhesión de brackets sobre dientes con y sin blanqueamiento (spa)
info:eu-repo/semantics/bachelorThesis (eng)
Universidad Privada Antenor Orrego. Facultad de Medicina Humana (spa)
Estomatología (spa)
Título Profesional (spa)
Cirujano Dentista (spa)
Privada asociativa



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.