Title: Resistencia a la compresión de cuatro resinas compuestas nanohibridas con circonio utilizados en Perú – 2021
Other Titles: Compressive strength of four nanohyride composite resins with zirconium used in Peru – 2021
Advisor(s): Cueva Buendía, Luis Alberto
OCDE field: http://purl.org/pe-repo/ocde/ford#3.02.14
Issue Date: 18-Dec-2021
Institution: Universidad Privada de Huancayo Franklin Roosevelt
Abstract: La investigación es aplicada y respondió a un diseño experimental in vitro, prospectivo. La muestra estuvo conformada por 40 cilindros de 4 mm de diámetro por 10 mm de alto; dividida en 4 grupos de resinas compuestas nanohíbridas con circonio; Forma® Ultradent, Vitra® de FGM, Estelite® Alpha de Tokuyama y Palfique® 5XL de Tokuyama. Se utilizaron las pruebas estadísticas de Kolmogorov Smirnov para la normalidad y la prueba de ANOVA, como la prueba de Tukey para la relación entre dos grupos. Los resultados develaron un 95% de nivel de confianza y una significancia de α=0.05 con la prueba de análisis de varianza (ANOVA), se evidenció un p=0.082 > 0.05; por lo que no se refleja significancia estadística, constatándose una mayor resistencia numérica en la resina compuesta nanohíbrida con circonio de Forma® Ultradent con un 216.26 Mpa. Se concluye que todas las resinas odontológicas utilizadas en Perú presentan la misma resistencia compuestas nanohíbridas con circonio

The research is applied and responded to an in vitro, prospective experimental design. The sample consisted of 40 cylinders of 4 mm diameter by 10 mm high; divided into 4 groups of nanohybrid composite resins with zirconium; Forma® Ultradent, Vitra® from FGM, Estelite® Alpha from Tokuyama and Palfique® 5XL from Tokuyama. The Kolmogorov Smirnov statistical test for normality and the ANOVA test were used, as was the Tukey test for the relationship between two groups. The results revealed a 95% confidence level and a significance of α=0.05 with the analysis of variance test (ANOVA), a p=0.082 > 0.05 was evidenced; therefore, statistical significance is not reflected, noting a higher numerical strength in the nanohybrid composite resin with zirconia of Forma® Ultradent with a 216.26 Mpa. It is concluded that all the dental resins used in Peru present the same resistance as the nanohybrid composite resins with zirconium
Discipline: Escuela Profesional de Estomatología
Grade or title grantor: Universidad Privada de Huancayo Franklin Roosevelt. Ciencias de la Salud
Grade or title: Cirujano Dentista
Juror: Cueva Buendía, Luis Alberto; Pariajulca Fernandez, Israel Robert; Bonilla Cairo, Pablo Santiago; Travesaño Arteaga, Oscar Raúl
Register date: 7-Mar-2022; 7-Mar-2022



This item is licensed under a Creative Commons License Creative Commons