Title: Resistencia a compresión de un mortero cemento-arena (1:3 y 1:4) al reemplazar distintos porcentajes de arena de rio por arena de duna (10 y 20%)
Advisor(s): Ravines Azañero, Irene Del Rosario
OCDE field: https://purl.org/pe-repo/ocde/ford#2.01.01
Issue Date: 6-Nov-2017
Institution: Universidad Privada del Norte
Abstract: RESUMEN La presente investigación logró comparar la resistencia a compresión de un mortero cementoarena (1:3 y 1:4) al reemplazar distintos porcentajes de arena de río por arena de duna (10 y 20%). Para esto se ha analizado las propiedades físicas de las arenas de río y duna como son contenido de humedad (W = 5.90% para la arena de río y W = 1.03% para la arena de duna), granulometría (MF = 2.33 para la arena de río y MF = para la arena de duna), peso unitario suelto y compactado (PUSS = 1.70 y PUCS = 1.82 g/cm3 para la arena de río y PUSS = 1.38 g/cm3 y PUCS = 1.57 g/cm3 para la arena de duna), peso específico y porcentaje de absorción que sirvió para diseñar el mortero, adicionalmente se realizó un estudio químico de sales agresivas a la arena de duna para determinar la cantidad de cloruros y sulfatos que contiene; consecuentemente se realizaron las probetas de mortero y se ensayaron en resistencia a compresión a los 3, 7 y 28 días de curado. Con la investigación se determinó: para la dosificación cemento-arena 1:3 con reemplazo del 10% de arena de duna la resistencia disminuye en 6.88% y con reemplazo del 20% de arena de duna la resistencia disminuye en 7.70%; para la dosificación cemento-arena 1:4 con reemplazo del 10% de arena de duna la resistencia disminuye en 3.13% y con reemplazo del 20% de arena de duna la resistencia disminuye en 9.20%; determinándose que la proporción 1:4 posee mejores características.

ABSTRACT The present research seeks to compare the compressive strength of a cement-sand mortar (1: 3 and 1: 4) by replacing different percentages of river sand with sand dune (10 and 20%). For this the physical properties of the river and dune sands have been analyzed as they are moisture content (W = 5.90% for the river sand and W = 1.03% for the sand of dune), granulometry (MF = 2.33 for the sand (PUSS = 1.70 and PUCS = 1.82 g/cm3 for river sand and PUSS = 1.38 g/cm3 and PUCS = 1.57 g/cm3 for the sand dune), specific weight and percentage of absorption that served to design the mortar, in addition a chemical study of aggressive salts to the dune sand was carried out to determine the amount of chloride and sulfates it contains; consequently the test tubes were made and tested in compression resistance at 3, 7 and 28 days of curing. With the research it was determined: for the 1: 3 cement-sand dosage with replacement of 10% of sand dune the resistance decreases in 6.88% and with replacement of 20% of dune sand the resistance decreases in 7.70%; for the 1: 4 cement-sand dosage with 10% sand dune replacement the resistance decreases by 3.13% and with a 20% sand dune replacement the resistance decreases by 9.20%.
Note: Cajamarca
Discipline: Ingeniería Civil
Grade or title grantor: Universidad Privada del Norte. Facultad de Ingeniería
Grade or title: Ingeniero Civil
Juror: Aguilar Aliaga, Orlando; Sánchez Portal, Fabián Sebastián; Alva Sarmiento, Anita Elízabet
Register date: 14-Nov-2017; 14-Nov-2017



This item is licensed under a Creative Commons License Creative Commons