La presente investigación tiene como objetivo principal determinar cómo varía las propiedades físico-mecánicas de un concreto f'c=210 kg/cm2 al ser sometido a una temperatura de 800°C y luego ser enfriado con agua y espuma respecto a una muestra control, la metodología del diseño que se empleo fue experimental, donde se empleó probetas cilíndricas de 15 cm X 30 cm elaborados de concreto que contenía cemento tipo IP, agregado grueso de la cantera de Vicho y agregado fino de la cantera de Vicho y Cunyac todos estos pasando por los diferentes ensayos correspondientes para la elaboración del diseño de mezcla. Las probetas de concreto se dividieron en sub grupos (muestras patrón, quemadas y enfriadas con agua, quemadas y enfriadas con espuma) para luego hacer su análisis en peso, volumen, resistencia a la compresión y módulo de elasticidad. Finalmente, después de realizar las pruebas y hacer un análisis y comparación de datos se llegó a la conclusión que efectivamente el concreto f'c=210 kg/cm2 al ser sometido a una temperatura de 800°C y luego ser enfriado con agua y espuma respecto a una muestra control tiene una alteración en sus propiedades físico – mecánicas siendo los resultados diferentes dependiendo del agente enfriante, observando que la variación más significativa es al ser enfriado con espuma. Lo que nos da a conocer que el concreto de una estructura que fue incendiada es más insegura y perdió sus propiedades físico – mecánicas en mayor dimensión si los primeros respondedores tomaron la decisión de utilizar la espuma, esto también ayuda a los primeros respondedores de ser más estrictos en las medidas de seguridad si optan por utilizar la espuma en una estructura.
The main objective of the present investigation is to determine how the physical-mechanical properties of a concrete f'c=210 kg/cm2 vary when it is subjected to a temperature of 800°C and then cooled with water and foam in comparison with a control. shows. . The design methodology used was experimental, where 15 cm cylindrical specimens were used through the different corresponding tests to prepare the mixture design. The concrete samples were divided into subgroups (standard samples, burned and water-cooled, burned and foam-cooled) and then analyzed for weight, volume, compressive strength and modulus of elasticity. Finally, after carrying out the tests, analyzing and comparing the data, it was concluded that the concrete f'c=210 kg/cm2 when subjected to a temperature of 800°C and then cooled with water and foam. Compared with a control sample, it presents an alteration in its physical-mechanical properties, the results being different depending on the cooling agent, observing that the most significant variation is when cooled with foam, which indicates that the concrete of a structure that was burned is more unsafe and loses its physical-mechanical properties to a greater extent if the lifeguards made the decision to use the foam. This also helps the lifeguards to be more strict in safety measures if they choose to use the foam in a structure. . (en_US)
application/pdf
spa
Universidad Andina del Cusco
info:eu-repo/semantics/openAccess
http://creativecommons.org/licenses/by-nc-nd/2.5/pe/
Temperatura
Resistencia a la compresión
Módulo de elasticidad
Probeta de concreto
Evaluación comparativa de las propiedades físico-mecánicas de un concreto f’c= 210 kg/cm², sometido a una temperatura de 800°c y luego ser enfriado con agua y espuma respecto a una muestra control, Cusco 2023
info:eu-repo/semantics/bachelorThesis
Universidad Andina del Cusco. Facultad de Ingeniería y Arquitectura
Ingeniería Civil
Ingeniero Civil
PE
https://purl.org/pe-repo/ocde/ford#2.01.01
https://purl.org/pe-repo/renati/level#tituloProfesional
46086133
https://orcid.org/0000-0002-3510-5043
71428792
73578185
732016
Alvarez Monterola, Walter Roberto
Ascue Escalante, Kildare Jussety
Calderon Gonzales, Werner Alfonso
https://purl.org/pe-repo/renati/type#tesis
Privada asociativa



This item is licensed under a Creative Commons License Creative Commons