En esta investigación llevada a cabo en la ciudad del Cusco, se examinaron las propiedades físicas y mecánicas de un mortero de cemento blanco (mortero patrón), al que se le añadió un pigmento fotoluminiscente (Aluminato de estroncio) en una proporción del 30% respecto al contenido del cemento y se incorporó también vidrio molido reciclado en diferentes porcentajes (5%, 10% y 15%) en relación al contenido del agregado fino. Se evaluaron sus propiedades en estado endurecido como la resistencia a la compresión, resistencia a la flexión, resistencia a la adherencia y luminosidad, así como la fluidez en estado fresco. Se realizaron ensayos previos como el análisis granulométrico, densidad aparente, contenido de humedad, densidad del cemento y consistencia de la pasta de cemento para realizar el diseño de mezcla. El agregado fino es de la cantera de Cunyac y el cemento empleado es el cemento blanco Pórtland tipo I, la evaluación de los morteros fueron a las edades de 3,7 y 28 días de curado. El vidrio molido se incorporó debido a sus propiedades mecánicas elevadas, por lo tanto, se esperaba que las propiedades mecánicas del mortero incrementen, mientras que el pigmento fotoluminiscente se añadió para mejorar la luminosidad. Se siguieron las Normas Técnicas Peruanas (NTP) y normas internaciones (UNE, ASTM, NCh) para la selección de muestras, análisis y ensayos. Los resultados indicaron que el mortero fotoluminiscente añadido con 15% de vidrio molido reciclado, mostró la mayor resistencia a la compresión y adherencia (199.33 Kg/cm 2 y 2 4.97 Kg/cm respectivamente). El mortero fotoluminiscente con 5% de vidrio molido reciclado, presentó la mayor resistencia a la flexión (73.73 Kg/cm 2 ). Sin embargo, no se detectaron diferencias significativas en la luminosidad entre los morteros fotoluminiscentes elaborados. (es_PE)
In this research conducted in the city of Cusco, the physical and mechanical properties of a white cement mortar (standard mortar) were examined. A photoluminescent pigment (Strontium Aluminate) was added to the mortar in a proportion of 30% relative to the cement content, and recycle crushed glass was also incorporated in different percentages (5%, 10% and 15%) in relation to the dine aggregate content. Properties in the hardened state were evaluated, such as compressive strength, flexural strength, bond strength and luminosity, as well as fresh as state fluidity. Preliminary tests were conducted, including particle size analysis, bulk density, moisture content, cement density and paste consistency, to design the mixture. The fine aggregate was sourced from the Cunyac quarry and Portland Type I white cement was used. The evaluation of the mortars was carried out at ages of 3, 7 and 28 days of curing. Crushed glass was incorporated due to its high mechanical properties, thus an increase in the mechanical properties of the mortar was expected, while the photoluminescent pigment was added to enhance luminosity. Peruvian Technical Standards (NTP) and international standards (UNE, ASTM, NCh) were followed for sample selection, analysis and testing. The results indicated that the photoluminescent mortar with 15% recycled crushed glass showed the highest compressive and bond strength (199.33 Kg/cm 2 and 4.97 Kg/cm 2 , respectively). The photoluminescent mortar with 5% recycled crushed glass exhibited the highest flexural strength (73.73 Kg/cm 2 ). However, no significant differences in luminosity were detected among the produced photoluminescent mortars. (en_US)
application/pdf (es_PE)
spa (es_PE)
Universidad Andina del Cusco (es_PE)
info:eu-repo/semantics/restrictedAccess (es_PE)
https://creativecommons.org/licenses/by-nc-nd/4.0/ (es_PE)
Mortero (es_PE)
Aluminato de estroncio (es_PE)
Fluidez (es_PE)
Vidrio molido reciclado (es_PE)
Análisis comparativo de la resistencia a la compresión, adherencia, fluidez y fotoluminiscencia de un mortero patrón con respecto al mortero elaborado con cemento blanco adicionado con aluminato de estroncio al 30% y vidrio molido reciclado al 5%, 10% y 15%, Cusco 2023 (es_PE)
info:eu-repo/semantics/bachelorThesis (es_PE)
Universidad Andina del Cusco. Facultad de Ingeniería y Arquitectura (es_PE)
Ingeniería Civil (es_PE)
Ingeniero Civil (es_PE)
PE (es_PE)
https://purl.org/pe-repo/ocde/ford#2.01.01 (es_PE)
https://purl.org/pe-repo/renati/level#tituloProfesional (es_PE)
44982950
https://orcid.org/0000-0002-7793-8844 (es_PE)
72029774
72741266
732016 (es_PE)
Arohuanca Sosa, Rode Luz
Alvarez Espinoza, Jorge
Cana Paullo, Hugo
Gonzalez Mamany, Nico Yheison
https://purl.org/pe-repo/renati/type#tesis (es_PE)
Privada asociativa



This item is licensed under a Creative Commons License Creative Commons