In this research the influence that exerts the rapid cooling of preheated fly ashes at 650 ° C, as well as the grinding of the same, on the compressive strength of geopolymers based on fluidized bed carbon ash (FBCA) was evaluated. These two operations were carried out to increase the formation of amorphous phases and increase the specific surface area of the ashes, respectively. The FBCA was subjected to a pre-calcination at 650 ° C in order to eliminate the remains of charcoal that could not be burned in the cauldron. For the geopolimerization of the FBCA, sodium silicate with silica module 2.5 and a solution of 10 M NaOH were used. The cubic samples, obtained in molds of 50x50x50 mm, were thermally cured at 80 ° C for 12 and 24 h. It was determined that the greatest effect on the resistance was obtained with the grinding during 6 h of the FBCA precalcined at 650 ° C, achieving resistance in the order of 92 MPa (es_PE)
En la presente investigación se evaluó la influencia que ejerce, tanto el enfriamiento rápido de las cenizas volantes precalentadas a 650°C como la molienda de las mismas, en la resistencia a la compresión de geopolímeros basados en cenizas de carbón de calderos de lecho fluidizado (CCLF). Esas dos operaciones fueron efectuadas para incrementar la formación de fases amorfas y aumentar el área superficial específica de las cenizas, respectivamente. A las CCLF, se le sometió a una pre-calcinación a 650°C, a fin de eliminar los restos de carbón que no se lograron quemar en el caldero. Para la geopolimerización de las CCLF, se utilizó silicato de sodio de módulo de sílice 2.5 y una solución de NaOH 10 M. Las probetas cúbicas, obtenidas en moldes de 50x50x50 mm, fueron curadas térmicamente a 80°C por 12 y 24 h. Se determinó que el mayor efecto sobre la resistencia se logró con la molienda durante 6 h, de las CCLF precalcinadas a 650°C, lográndose resistencias del orden de 92 MPa (es_PE)
Tesis (es_PE)
spa (es_PE)
Universidad Nacional de Trujillo (es_PE)
info:eu-repo/semantics/openAccess (es_PE)
http://creativecommons.org/licenses/by-nc-nd/2.5/pe/ (es_PE)
Universidad Nacional de Trujillo (es_PE)
Repositorio institucional - UNITRU (es_PE)
Geopolímero (es_PE)
Cenizas de lecho fluidizado (es_PE)
Temple (es_PE)
Molienda (es_PE)
Tiempo de curado (es_PE)
Temperatura de curado (es_PE)
Resistencia a la compresión (es_PE)
Efecto del temple y la modalidad de cenizas volantes pretratadas térmicamente para la elaboración de geopolímeros, a una relación molar de NaOH y Na2SiO3 constante (es_PE)
info:eu-repo/semantics/bachelorThesis (es_PE)
Universidad Nacional de Trujillo. Facultad de Ingeniería Química (es_PE)
Ingeniería Ambiental (es_PE)
Título Profesional (es_PE)
Ingeniero Ambiental (es_PE)
Pública



This item is licensed under a Creative Commons License Creative Commons