Título: Estudio comparativo de las propiedades mecánicas de los cordones y las juntas soldadas multipase con electrodos (SMAW) de diferente aplicación
Asesor(es): Sarmiento Sarmiento, Enrique
Campo OCDE: http://purl.org/pe-repo/ocde/ford#2.03.01
Fecha de publicación: 2023
Institución: Universidad Nacional de Ingeniería
Resumen: La investigación que se explica a continuación se realizó con el propósito de comparar si los valores de las propiedades mecánicas, de los cordones de soldadura obtenidos al soldar utilizando combinaciones de materiales de aporte (electrodos), son iguales a los valores con las que se diseña o califica los WPS que generalmente es el valor promedio de las propiedades que indica la norma. La experiencia se realizó bajo un enfoque cuantitativo de nivel explicativo con un diseño experimental basado en ensayo de laboratorio y alcance correlacional, para los ensayos se procedió a preparar 8 cupones los cuales fueron elaborados utilizando electrodos determinados antes de la fabricación de cupones, teniendo como variable independiente los cordones y juntas soldadas de cada cupón, y como variables dependientes las propiedades mecánicas y químicas Luego de la tabulación de datos obtenidos de las normas utilizadas, con los cuales se obtuvieron los valores que usualmente se utilizan, se procedió a realizar los ensayos de acuerdo a las normas establecidas AWS D 1.1 y AWS A 5.1 AWS 5.5, obteniéndose los datos experimentales para luego ser comparados con los obtenidos con la norma, y luego de ser analizadas estadísticamente con la prueba de Pearson el cual me permitió afirmar que los valores de las propiedades mecánicas, obtenidas en los cordones experimentalmente no son iguales a los usados generalmente.

The research explained below was carried out with the purpose of comparing whether the values of the mechanical properties of the weld beads obtained when welding using combinations of filler materials (electrodes) are equal to the values with which they are designed. or qualifies the WPS, which is generally the average value of the properties indicated by the standard. The experience was carried out under a quantitative approach at an explanatory level with an experimental design based on laboratory testing and correlational scope. For the tests,8 coupons were prepared, which were prepared using electrodes determined before the coupon manufacturing, taking as a variable independently the beads and welded joints of each coupon, and as dependent variables the mechanical and chemical properties After the tabulation of data obtained from the standards used, with which the values that are usually used were obtained, the tests were carried out according to the established standards AWS D 1.1 and AWS A 5.1 AWS 5.5, obtaining the experimental data to then be compared with those obtained with the standard, and after being statistically analyzed with the Pearson test which allowed me to affirm that the values of the mechanical properties, obtained in the cords experimentally, are not equal to those generally used.
Disciplina académico-profesional: Ingeniería Mecánica
Institución que otorga el grado o título: Universidad Nacional de Ingeniería. Facultad de Ingeniería Mecánica
Grado o título: Ingeniero Mecánico
Jurado: Padilla Ríos, Aurelio Marcelo; Silva Vásquez, Wilson José
Fecha de registro: 25-jul-2024



Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons Creative Commons