Title: Estudio del concreto con aditivo acelerante y cemento Portland tipo I
Advisor(s): Barzola Gastelú, Carlos Armando
OCDE field: http://purl.org/pe-repo/ocde/ford#2.01.01
Issue Date: 2022
Institution: Universidad Nacional de Ingeniería
Abstract: En esta investigación se explica la utilización del aditivo acelerante que tiene en las propiedades del concreto con cemento portland tipo I. Ante la necesidad de elevar la eficiencia en la industria de la construcción, dándole mayor rotación a los encofrados, de modo que, para lograr este propósito se requiere que el concreto adquiera la resistencia a la compresión requerida en menor tiempo. Para que el concreto obtenga mayor velocidad de desarrollo de resistencias iniciales se requiere alterar la curva de desarrollo de la resistencia y para lo cual se requiere el uso de un aditivo acelerante. Para realizar la investigación se realizó en tres relaciones A/C: 0.60, 0.65 y 0.70 con tres dosificaciones de aditivo acelerante de 250 ml, 375 ml y 500 ml por bolsa de cemento. En A/C 0.60, 0.65 y 0.70 con una dosificación de 500 ml, que es la que da mejores resultados, aumenta la resistencia a la compresión en 163.57%, 160.01% y 161.79% a un día y en 126.40%, 126.74% y 108.05% a los 28 días respectivamente, respecto al concreto patrón 100%. En A/C 0.60, 0.65 y 0.70 con una dosificación de 500 ml, que es la que da mejores resultados, disminuye el tiempo de fraguado inicial en 84.52%, 95.70% y 86.79% respectivamente, respecto al concreto patrón 100%. En A/C 0.60, 0.65 y 0.70 con una dosificación de 500 ml, que es la que da mejores resultados, disminuye el tiempo de fraguado final en 87.81%, 90.95% y 80.48% respectivamente respecto al concreto patrón 100%. El aditivo acelerante causa efecto en acelerar las resistencias y en disminuir el tiempo de fraguado inicial y final, lo cual es el objetivo de la investigación.

This research explains the effect of the accelerating additive that is has on the properties of concrete with Portland cement type I. Given the need to increase productivity in the construction industry, giving more rotation to the formwork, so that, to achieve this purpose it is required that the concrete acquires compressive strength in less time. In order for the concrete to obtain high initial strengths, it is necessary to alter the strength development curve and for which the use of an accelerating admixture is required. To carry out the investigation, three A/C ratios were carried out: 0.60, 0.65 and 0.70 with three dosages of accelerating additive of 250 ml, 375 ml and 500 ml per bag of cement. In A/C 0.60, 0.65 and 0.70 with a dosage of 500 ml, which is the one that gives the best results, the compressive strength increases by 163.57%, 160.01% and y 161.79% at one day and by 126.40%, 126.74% and 108.05% at 28 días respectively, with respect to the 100% standard concrete. In A/C 0.60, 0.65 and 0.70 with a dosage of 500 ml, which is the one that gives the best results, the initial setting time decreases by 84.52%, 95.70% and 86.79%, respectively, with respect to the 100% standard concrete. In A/C 0.60, 0.65 and 0.70 with a dosage of 500 ml, which is the one that gives the best results, the final setting time decreases by 87.81%, 90.95% and 80.48%, respectively, with respect to the 100% standard concrete. The accelerating additive has an effect in accelerating the resistance and in reducing the initial and final setting time, which is the objective of the investigation.
Discipline: Ingeniería Civil
Grade or title grantor: Universidad Nacional de Ingeniería. Facultad de Ingeniería Civil
Grade or title: Ingeniero Civil
Juror: Villegas Martínez, Carlos Alberto; Arrieta Freyre, Javier Eduardo
Register date: 31-May-2023



This item is licensed under a Creative Commons License Creative Commons