La construcción es una actividad de alto impacto económico y tecnológico con una elevada necesidad de mejora continua; en este contexto, los materiales desempeñan un rol importante en la calidad de las obras civiles. Enfocada la investigación en la mejora del concreto como elemento de mayor trascendencia en la construcción, se identificó la problemática recaída en el desconocimiento de la influencia del tereftalato de polietileno en la resistencia a la compresión del concreto 280 Kg/cm2. Para dar una solución a la problemática, se ensayaron diversas proporciones de dicho plástico como adición del concreto fresco, midiendo luego su resistencia a la compresión a los siete, 14 y 28 días de curado. Los resultados muestran que pequeñas proporciones de dicho plástico, específicamente la de 1,0% en peso respecto al cemento de diseño, logró una mejora significativa de un 45,26% al compararla con el concreto patrón a los 28 días. El resultado obtenido permitió validar y aceptar la hipótesis de trabajo que, como respuesta tentativa, había previsto al tereftalato de polietileno como adición influyente y significativa. El resultado abona en la aclaración de los dispares resultados obtenidos por diferentes investigadores sobre el tema, aportando un resultado fielmente ajustado a los datos encontrados. (es_PE)
Construction is an activity with high economic and technological impact with a high need for continuous improvement; In this context, materials play an important role in the quality of civil works. With the research focused on the improvement of concrete as an element of greatest importance in construction, the problematic relapse into ignorance of the influence of polyethylene terephthalate on the compressive strength of concrete 280 Kg/cm2 was identified. To provide a solution to the problem, various proportions of said plastic were tested as an addition to the fresh concrete, then measuring its compressive strength after seven, 14 and 28 days of curing. The results show that small proportions of said plastic, specifically 1.0% by weight with respect to the design cement, achieved a significant improvement of 45.26% when compared to the standard concrete after 28 days. The result obtained allowed us to validate and accept the working hypothesis that, as a tentative response, had foreseen polyethylene terephthalate as an influential and significant addition. The result contributes to the clarification of the disparate results obtained by different researchers on the subject, providing a result faithfully adjusted to the data found (es_PE)
Tesis (es_PE)
application/pdf (es_PE)
spa (es_PE)
Universidad Privada Antenor Orrego (es_PE)
T_CIVILP_082
info:eu-repo/semantics/openAccess (es_PE)
https://creativecommons.org/licenses/by/4.0/ (es_PE)
Concreto 280 Kg/cm (es_PE)
Resistencia de la Compresión (es_PE)
Influencia del tereftalato de polietileno en la resistencia a la compresión del concreto 280 Kg/cm2, Piura, 2023 (es_PE)
info:eu-repo/semantics/bachelorThesis (es_PE)
Universidad Privada Antenor Orrego. Facultad de Ingenieria (es_PE)
Ingenieria Civil (es_PE)
Ingeniero Civil (es_PE)
PE (es_PE)
https://purl.org/pe-repo/ocde/ford#2.01.00 (es_PE)
https://purl.org/pe-repo/renati/level#tituloProfesional (es_PE)
02805945
https://orcid.org/0000-0002-0498-9544 (es_PE)
72455073
72732090
732016 (es_PE)
Ramal Montejo, Rodolfo Enrique
Chan Heredia, Miguel Ange
Valdiviezo Castillo, Krissia del Fatima
https://purl.org/pe-repo/renati/type#tesis (es_PE)
Privada asociativa



This item is licensed under a Creative Commons License Creative Commons