Title: Estudio comparativo de la resistencia a la compresión del concreto utilizando acero reciclado como agregado grueso Iquitos - 2023
Advisor(s): García Langer, Carol Begoña
OCDE field: https://purl.org/pe-repo/ocde/ford#2.01.00
Issue Date: 16-Jan-2024
Institution: Universidad Científica del Perú
Abstract: La presente investigación, tiene como objetivo la comparación de los ensayos de resistencia a la compresión de un concreto convencional 210kg/cm2, con la adición de acero reciclado como parte del agregado grueso y una a relación A/C = 0.66. la muestra estuvo conformada por 72 especímenes , los cuales se realizaron en el laboratorio de la universidad científica del Perú ( UCP), mismas que fueron curados durante 28 días y se sometieron a la prueba de resistencia a la compresión en edades de 3, 7, 14, y 28 días. se aplicó la estadística descriptiva para el procesamiento y análisis de los resultados; y se comprobó la hipótesis al momento de ver y analizar los resultados obtenidos de los ensayos que se realizaron. los resultados de los ensayos que se vio en este estudio arrojaron que el concreto convencional ( utilizando piedra chancada de ¾ ) alcanzo la mayor resistencia siendo este 279kg/cm2, superando al diseño al cual se le adiciono ( acero reciclado) alcanzando 257kg/cm2, siendo supero por el diseño con piedra chancada en 22kg/cm2. Analizando los resultados todos son aceptables ya que los mismos sobrepasan al f’c de diseño o concreto patrón. Finalmente, con la investigación realizada se puede concluir; que se si se puede utilizar el acero reciclado como parte del agregado grueso, fomentando así en el mundo de la construcción la cultura del reciclaje y de esa manera co0ntribuir con el medio ambiente. Por lo tanto, si existe diferencia al utilizar acero reciclado como parte del agregado grueso en el diseño de mezcla la cual responde a nuestra hipótesis.

The objective of this research is to compare the compressive strength tests of a conventional 210kg/cm2 concrete, with the addition of recycled steel as part of the coarse aggregate and a W/C ratio = 0.66. The sample was made up of 72 specimens, which were made in the laboratory of the Scientific University of Peru (UCP), which were cured for 28 days and underwent the compression resistance test at ages of 3, 7, 14, and 28 days. Descriptive statistics were applied for the processing and analysis of the results; and the hypothesis was proven when viewing and analyzing the results obtained from the tests that were carried out. The results of the tests seen in this study showed that conventional concrete (using ¾ crushed stone) achieved the highest resistance, being 279kg/cm2, surpassing the design to which it was added (recycled steel) reaching 257kg/cm2. being surpassed by the design with crushed stone at 22kg/cm2. Analyzing the results, they are all acceptable since they exceed the f'c of the design or standard concrete. Finally, with the research carried out it can be concluded; I know if recycled steel can be used as part of the coarse aggregate, thus promoting the culture of recycling in the world of construction and thus contributing to the environment. Therefore, there is a difference when using recycled steel as part of the coarse aggregate in the mix design which responds to our hypothesis.
Discipline: Ingeniería Civil
Grade or title grantor: Universidad Científica del Perú. Facultad de Ciencias e Ingeniería
Grade or title: Ingeniero Civil
Juror: Wong Ramírez, Félix; Ocaña Aponte, Juan Jesús; Arévalo Flores, Jefree Stefano
Register date: 14-Mar-2024



This item is licensed under a Creative Commons License Creative Commons