La investigación “tuvo como objetivo determinar la influencia del aditivo Chema Estruct en 1.0%, 1.5% y 2.0% y la fibra de vidrio en 0.5%. 1.0% y 1.5% sobre la resistencia a la compresión y asentamiento de un concreto 280 kg/cm2 , Trujillo.” “La investigación fue aplicada, “de diseño experimental, para ello se usó fichas validadas como instrumentos que se utilizaron para recolectar los datos, la muestra estuvo compuesta por diversas probetas de concreto patrón y probetas con diferentes proporciones de Chema Estruct (1.0%, 1.5% y 2.0%) y fibras de vidrio (0.5%, 1.0% y 1.5%). En total, se elaboraron 144 probetas de dimensiones 100 mm x 200 mm con Cemento Portland Compuesto Tipo ICo, para llevar a cabo los diversos ensayos mencionados. Estas fueron analizadas a tres edades distintas durante el período de curado del concreto, específicamente a los 7, 14 y 28 días, como se muestra en la tabla siguiente.” Obteniendo como resultados que “conformen aumenta el porcentaje de aditivo Chema Estruct aumenta la trabajabilidad del concreto, pero conforme aumenta el porcentaje de fibra de vidrio disminuye la trabajabilidad. Y con respecto a la resistencia a la compresión, a los 28 días de curado se obtuvo que la adición de 1.5% de aditivo Chema Estruct con 1.0% de fibra de vidrio se obtuvo un valor de 363.81 kg/cm2 siendo la resistencia más alta, siendo estos valores los óptimos para mejorar la resistencia del concreto a 28 días de curado.” Concluyendo que, “la adición de aditivo Chema Estruct y fibra de vidria influyen positivamente sobre las propiedades físico mecánicas de un concreto 280 kg/cm2 , Trujillo (es_PE)
The research aimed ""to determine the influence of the Chema Estruct additive at 1.0%, 1.5%, and 2.0% and fiberglass at 0.5%, 1.0%, and 1.5% on the compressive strength and slump of a 280 kg/cm² concrete in Trujillo."" The study was applied and followed an experimental design. “Validated data collection sheets were used as instruments, and the sample consisted of various standard concrete specimens along with specimens containing different proportions of Chema Estruct (1.0%, 1.5%, and 2.0%) and fiberglass (0.5%, 1.0%, and 1.5%). In total, 144 specimens measuring 100 mm x 200 mm were prepared with Type ICo Portland Composite Cement to conduct the various tests. These specimens were analyzed at three different ages during the curing period, specifically at 7, 14, and 28 days, as shown in the following table.” The results indicated that ""as the percentage of Chema Estruct additive increases, the workability of the concrete improves, while as the percentage of fiberglass increases, the workability decreases. Regarding compressive strength, at 28 days of curing, a combination of 1.5% Chema Estruct additive and 1.0% fiberglass yielded a value of 363.81 kg/cm², representing the highest compressive strength and the optimal values to enhance concrete strength at 28 days of curing."" The study concluded that ""the addition of Chema Estruct additive and fiberglass positively influences the physical-mechanical properties of a 280 kg/cm² concrete in Trujillo (es_PE)
Tesis (es_PE)
application/pdf (es_PE)
spa (es_PE)
Universidad Privada Antenor Orrego (es_PE)
T_CIVIL_2685
info:eu-repo/semantics/openAccess (es_PE)
https://creativecommons.org/licenses/by/4.0/ (es_PE)
Concreto (es_PE)
aditivo (es_PE)
compresión (es_PE)
Influencia del Chema Estruct y fibra de vidrio sobre la compresión y asentamiento de un concreto 280 kg/cm2, Trujillo (es_PE)
info:eu-repo/semantics/bachelorThesis (es_PE)
Universidad Privada Antenor Orrego. Facultad de Ingeniería (es_PE)
Ingeniería Civil (es_PE)
Ingeniero Civil (es_PE)
PE (es_PE)
https://purl.org/pe-repo/ocde/ford#2.01.00 (es_PE)
https://purl.org/pe-repo/renati/level#tituloProfesional (es_PE)
41356105
https://orcid.org/0000-0003-2772-4829 (es_PE)
47833429
45608080
732016 (es_PE)
Durand Orellana, Rocío del Pilar
Sánchez Malpica, Carmen Esperanza
Henríquez Ulloa, Juan Paul Edward
https://purl.org/pe-repo/renati/type#tesis (es_PE)
Privada asociativa



This item is licensed under a Creative Commons License Creative Commons