Título: Estudio de la densidad, porcentaje de absorción, y vacíos del concreto cemento – arena empleando la norma ASTM C 642, Iquitos - 2021
Asesor(es): Irigoin Cabrera, Ulises Octavio
Campo OCDE: https://purl.org/pe-repo/ocde/ford#2.01.00
Fecha de publicación: 24-jul-2021
Institución: Universidad Científica del Perú
Resumen: Estudio de la densidad, porcentaje de absorción, y vacíos del concreto cemento – arena empleando la norma ASTM C 642, Iquitos - 2021 Para el concreto cemento – arena cuyo uso predomina en la Selva Baja peruana, no existían estudios que evalúen las propiedades en estado endurecido de densidad, porcentaje de absorción y porosidad (porcentaje de vacíos), razón que justificó la realización de la presente investigación. Como materiales se utilizó arena fina de 1.27 de módulo de finura, cemento portland tipo GU (APU). Se elaboró 36 especímenes de concreto cemento – arena, de 4”x8”, preparados para 0.60, 0.65 y 0.70 de relaciones agua/cemento. Para determinar la resistencia a la compresión se utilizó la norma ASTM C 39, efectuándose la rotura de 5 especímenes por cada relación agua/cemento, a los 7 y 28 días. Para la determinación de la densidad, porcentaje de absorción y porosidad se empleó la norma ASTM C 642, efectuándose cada uno de estos ensayos en un solo espécimen a los 7 y 28 días. Y la realización de los ensayos complementarios para determinar el contenido de aire del concreto y la temperatura del concreto en estado recién mezclado mediante las normas ASTM C 138 y ASTM C 1064 respectivamente. De los resultados obtenidos, se puede concluir que, a mayor relación a/c, el concreto cemento – arena adquiere semejante densidad que el concreto normalizado, pero mayor absorción y porosidad, asimismo, menor resistencia a la compresión. Del análisis de los fragmentos resultantes de la rotura de cada probeta, la parte superior presentó baja densidad, alta absorción y alta porosidad, y, el fragmento inferior resultó poseer una mayor densidad, pero baja absorción y baja porosidad.

Study of the density, absorption percentage, and voids of cement-sand concrete using the ASTM C 642 standard, Iquitos - 2021 For cement-sand concrete, the use of which predominates in the Peruvian Low Forest, there were no studies evaluating the properties in the hardened state of density, percentage of absorption and porosity (percentage of voids), a reason that justified the conduct of the present investigation. The materials used were fine sand with a modulus of fineness of 1.27, portland cement type GU (APU). 36 4 "x8" cement-sand concrete specimens were made, prepared for 0.60, 0.65 and 0.70 water / cement ratios. To determine the compressive strength, the ASTM C 39 standard was used, breaking 5 specimens for each water / cement ratio, at 7 and 28 days. For the determination of density, absorption percentage and porosity, the ASTM C 642 standard was used, each of these tests being carried out on a single specimen at 7 and 28 days. And the performance of complementary tests to determine the air content of the concrete and the temperature of the concrete in the freshly mixed state by means of the ASTM C 138 and ASTM C 1064 standards respectively. From the results obtained, it can be concluded that, with a higher w / c ratio, cement-sand concrete acquires a similar density than normalized concrete, but greater absorption and porosity, as well as lower resistance to compression. From the analysis of the fragments resulting from the breakage of each specimen, the upper part presented low density, high absorption and high porosity, and the lower fragment turned out to have a higher density, but low absorption and low porosity.
Disciplina académico-profesional: Ingeniería Civil
Institución que otorga el grado o título: Universidad Científica del Perú. Facultad de Ciencias e Ingeniería
Grado o título: Ingeniero Civil
Jurado: Ocaña Aponte, Juan Jesús; Arévalo Flores, Jefree Stefano; Gallardo Sánchez, Nerea
Fecha de registro: 27-sep-2021



Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons Creative Commons